Name: ASTM D 2803 : 2009 : R2015
Brand: ASTM

ASTM D 2803 : 2009 : R2015

Superseded

View Superseded by

Standard Guide for Testing Filiform Corrosion Resistance of Organic Coatings on Metal

Superseded date

18-08-2020

Published date

01-06-2015

Publisher

American Society for Testing and Materials

CONTAINED IN VOL. 06.01, 2017 Defines three procedures for determining the susceptibility of organic-coated metal substrates to formation of filiform corrosion.

1.1This guide covers three procedures for determining the susceptibility of organic-coated metal substrates to formation of filiform corrosion.

1.2This guide is limited to the determination of whether filiform corrosion will occur between the organic coating and substrate.

1.3The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.

1.4This standard does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Note 1:Procedure B of this standard is equivalent to ISO 4623.

Committee	D 01
DocumentType	Guide
ProductNote	Reconfirmed 2015
PublisherName	American Society for Testing and Materials
Status	Superseded
SupersededBy	ASTM D 2803 : 2009 : R2020
Supersedes	ASTM D 2803 : 2009

ASTM D 3794 : 2018	Standard Guide for Testing Coil Coatings
ASTM D 1654 : 2008 : R2016 : EDT 1	Standard Test Method for Evaluation of Painted or Coated Specimens Subjected to Corrosive Environments
ASTM D 3322 : 1982 : R2017	Standard Practice for Testing Primers and Primer Surfacers Over Preformed Metal
ASTM D 6577 : 2015	Standard Guide for Testing Industrial Protective Coatings
ASTM D 3451 : 2006 : R2017	Standard Guide for Testing Coating Powders and Powder Coatings
ASTM D 6577 : 2015 : R2019	Standard Guide for Testing Industrial Protective Coatings

ASTM D 1005 : 1995 : R2020	Standard Test Method for Measurement of Dry-Film Thickness of Organic Coatings Using Micrometers
ASTM D 1730 : 2009 : R2014	Standard Practices for Preparation of Aluminum and Aluminum-Alloy Surfaces for Painting
ASTM D 1730 : 2003	Standard Practices for Preparation of Aluminum and Aluminum-Alloy Surfaces for Painting
ASTM D 823 : 1995	Standard Practices for Producing Films of Uniform Thickness of Paint, Varnish, and Related Products on Test Panels
ISO 4623-2:2016	Paints and varnishes Determination of resistance to filiform corrosion Part 2: Aluminium substrates
ASTM D 609 : 2017 : REDLINE	Standard Practice for Preparation of Cold-Rolled Steel Panels for Testing Paint, Varnish, Conversion Coatings, and Related Coating Products
ASTM D 1730 : 2009	Standard Practices for Preparation of Aluminum and Aluminum-Alloy Surfaces for Painting
ASTM D 1654 : 2005	Standard Test Method for Evaluation of Painted or Coated Specimens Subjected to Corrosive Environments
ASTM D 1005 : 1995 : R2001	Standard Test Method for Measurement of Dry-Film Thickness of Organic Coatings Using Micrometers
ASTM D 1730 : 1967 : R1998	Standard Practices for Preparation of Aluminum and Aluminum-Alloy Surfaces for Painting
ISO 4623-1:2000	Paints and varnishes Determination of resistance to filiform corrosion Part 1: Steel substrates
ISO 4628-10:2016	Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 10: Assessment of degree of filiform corrosion
ASTM D 1005 : 1995 : R2013	Standard Test Method for Measurement of Dry-Film Thickness of Organic Coatings Using Micrometers
ASTM D 7091 : 2013	Standard Practice for Nondestructive Measurement of Dry Film Thickness of Nonmagnetic Coatings Applied to Ferrous Metals and Nonmagnetic, Nonconductive Coatings Applied to Non-Ferrous Metals
ASTM D 1730 : 2009 : R2020	Standard Practices for Preparation of Aluminum and Aluminum-Alloy Surfaces for Painting
ASTM D 1654 : 2008 : R2016	Standard Test Method for Evaluation of Painted or Coated Specimens Subjected to Corrosive Environments
ASTM D 7091 : 2013 : REDLINE	Standard Practice for Nondestructive Measurement of Dry Film Thickness of Nonmagnetic Coatings Applied to Ferrous Metals and Nonmagnetic, Nonconductive Coatings Applied to Non-Ferrous Metals
ASTM D 1654 : 1992 : R2000	Standard Test Method for Evaluation of Painted or Coated Specimens Subjected to Corrosive Environments
ASTM D 7091 : 2012	Standard Practice for Nondestructive Measurement of Dry Film Thickness of Nonmagnetic Coatings Applied to Ferrous Metals and Nonmagnetic, Nonconductive Coatings Applied to Non-Ferrous Metals
ASTM E 104 : 2002	Standard Practice for Maintaining Constant Relative Humidity by Means of Aqueous Solutions
ASTM D 7091 : 2005	Standard Practice for Nondestructive Measurement of Dry Film Thickness of Nonmagnetic Coatings Applied to Ferrous Metals and Nonmagnetic, Nonconductive Coatings Applied to Non-Ferrous Metals
ASTM D 1005 : 1995 : R2007	Standard Test Method for Measurement of Dry-Film Thickness of Organic Coatings Using Micrometers
ASTM D 1654 : 2008	Standard Test Method for Evaluation of Painted or Coated Specimens Subjected to Corrosive Environments
ASTM D 1654 : 2008 : R2016 : EDT 1	Standard Test Method for Evaluation of Painted or Coated Specimens Subjected to Corrosive Environments
ASTM D 1005 : 1995	Standard Test Method for Measurement of Dry-Film Thickness of Organic Coatings Using Micrometers