ASTM D 7175 : 2015
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
Hardcopy , PDF
29-01-2024
English
05-08-2015
This test method covers the determination of the dynamic shear modulus and phase angle of asphalt binders when tested in dynamic (oscillatory) shear using parallel plate geometry.
1.1This test method covers the determination of the dynamic shear modulus and phase angle of asphalt binders when tested in dynamic (oscillatory) shear using parallel plate geometry. It is applicable to asphalt binders having dynamic shear modulus values in the range from 100 Pa to 10 MPa. This range in modulus is typically obtained between 4 and 88°C at 10 rad/s. This test method is intended for determining the linear viscoelastic properties of asphalt binders as required for specification testing and is not intended as a comprehensive procedure for the full characterization of the viscoelastic properties of asphalt binders.
1.2This standard is appropriate for unaged materials, material aged in accordance with Test Method D2872, material aged in accordance with Practice D6521, or material aged in accordance with both Test Method D2872 and Practice D6521. This procedure is limited to asphalt binders that contain particles with largest dimension less than 250 μm.
1.3The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.4This standard may involve hazardous materials, operations, and equipment. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
| Committee |
D 04
|
| DocumentType |
Test Method
|
| Pages |
16
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Superseded
|
| SupersededBy | |
| Supersedes |
| ASTM D 7552 : 2022 | Standard Test Method for Determining the Complex Shear Modulus (G*) of Asphalt Mixtures Using Dynamic Shear Rheometer |
| ASTM D 7173 : 2020 | Standard Practice for Determining the Separation Tendency of Polymer from Polymer-Modified Asphalt |
| ASTM D 7643 : 2022 | Standard Practice for Determining the Continuous Grading Temperatures and Continuous Grades for PG Graded Asphalt Binders |
| ASTM D 6626 : 2015 : R2021 | Standard Specification for Performance-Graded Trinidad Lake Modified Asphalt Binder |
| ASTM D 7654/D7654M : 2010 : R2018 | Standard Specification for Asphalt Used in Roofing Measured by Dynamic Shear Rheometer |
| ASTM D 7944 : 2022 | Standard Practice for Recovery of Emulsified Asphalt Residue Using a Vacuum Oven |
| ASTM D 7405 : 2020 | Standard Test Method for Multiple Stress Creep and Recovery (MSCR) of Asphalt Binder Using a Dynamic Shear Rheometer |
| ASTM D 8239 : 2021 : REV A | Standard Specification for Performance-Graded Asphalt Binder Using the Multiple Stress Creep and Recovery (MSCR) Test |
| ASTM D 4887/D4887M : 2011 : R2021 : EDT 1 | Standard Practice for Preparation of Viscosity Blends for Hot Recycled Asphalt Materials |
| ASTM D 7643 : 2016 | Standard Practice for Determining the Continuous Grading Temperatures and Continuous Grades for PG Graded Asphalt Binders |
| ASTM D 4887/D4887M : 2011 : R2016 | Standard Practice for Preparation of Viscosity Blends for Hot Recycled Asphalt Materials |
| ASTM D 7552 : 2009 : R2014 | Standard Test Method for Determining the Complex Shear Modulus (G*) Of Bituminous Mixtures Using Dynamic Shear Rheometer |
| ASTM D 6626 : 2015 | Standard Specification for Performance Graded Trinidad Lake Modified Asphalt Binder |
| ASTM D 7405 : 2015 | Standard Test Method for Multiple Stress Creep and Recovery (MSCR) of Asphalt Binder Using a Dynamic Shear Rheometer |
| ASTM D 7173 : 2014 | Standard Practice for Determining the Separation Tendency of Polymer from Polymer Modified Asphalt |
| ASTM D 8239 : 2018 | Standard Specification for Performance-Graded Asphalt Binder Using the Multiple Stress Creep and Recovery (MSCR) Test |
| ASTM D 2493/D2493M : 2016 | Standard Practice for Viscosity-Temperature Chart for Asphalt Binders |
| ASTM D 7944 : 2015 | Standard Practice for Recovery of Emulsified Asphalt Residue Using a Vacuum Oven |
| ASTM D 6373 : 2016 | Standard Specification for Performance Graded Asphalt Binder |
| ASTM D 8239 : 2023 | Standard Specification for Performance-Graded Asphalt Binder Using the Multiple Stress Creep and Recovery (MSCR) Test |
| ASTM D 8189 : 2019 | Standard Test Method for Tackiness of Asphalt Binders and Emulsified Asphalt Residue Using the Dynamic Shear Rheometer (DSR) |
| ASTM D 6626 : 2023 | Standard Specification for Performance-Graded Trinidad Lake Modified Asphalt Binder |
| ASTM D 6373 : 2013 | Standard Specification for Performance Graded Asphalt Binder |
| ASTM D 6521 : 2018 | Standard Practice for Accelerated Aging of Asphalt Binder Using a Pressurized Aging Vessel (PAV) |
| ASTM E 563 : 1997 | Standard Practice for Preparation and Use of an Ice-Point Bath as a Reference Temperature |
| ASTM D 6521 : 2019 : REV A | Standard Practice for Accelerated Aging of Asphalt Binder Using a Pressurized Aging Vessel (PAV) |
| ASTM D 2872 : 2019 | Standard Test Method for Effect of Heat and Air on a Moving Film of Asphalt (Rolling Thin-Film Oven Test) |
| ASTM D 6521 : 2008 | Standard Practice for Accelerated Aging of Asphalt Binder Using a Pressurized Aging Vessel (PAV) |
| ASTM D 6373 : 1999 | Standard Specification for Performance Graded Asphalt Binder |
| ASTM D 6373 : 2023 | Standard Specification for Performance-Graded Asphalt Binder |
| ASTM D 6373 : 2016 | Standard Specification for Performance Graded Asphalt Binder |
| ASTM D 2170 : 2001 : REV A : R2006 | Standard Test Method for Kinematic Viscosity of Asphalts (Bitumens) |
| ASTM D 2170 : 1995 | Standard Test Method for Kinematic Viscosity of Asphalts (Bitumens) |
| ASTM D 6521 : 2013 | Standard Practice for Accelerated Aging of Asphalt Binder Using a Pressurized Aging Vessel (PAV) |
| ASTM D 2170 : 2007 | Standard Test Method for Kinematic Viscosity of Asphalts (Bitumens) |
| ASTM E 77 : 2014 : EDT 1 | Standard Test Method for Inspection and Verification of Thermometers |
| ASTM D 2872 : 2012 : EDT 1 | Standard Test Method for Effect of Heat and Air on a Moving Film of Asphalt (Rolling Thin-Film Oven Test) |
| ASTM E 563 : 2022 | Standard Practice for Preparation and Use of an Ice-Point Bath as a Reference Temperature |
| ASTM D 6521 : 2022 | Standard Practice for Accelerated Aging of Asphalt Binder Using a Pressurized Aging Vessel (PAV) |
| ASTM D 2170 : 2001 : REV A | Standard Test Method for Kinematic Viscosity of Asphalts (Bitumens) |
| ASTM D 6373 : 2021 : REV A | Standard Specification for Performance-Graded Asphalt Binder |
| ASTM D 2872 : 2012 | Standard Test Method for Effect of Heat and Air on a Moving Film of Asphalt (Rolling Thin-Film Oven Test) |
| ASTM E 563 : 2011 : R2016 | Standard Practice for Preparation and Use of an Ice-Point Bath as a Reference Temperature |
| ASTM D 2872 : 2021 | Standard Test Method for Effect of Heat and Air on a Moving Film of Asphalt (Rolling Thin-Film Oven Test) |
| ASTM D 6521 : 2005 | Standard Practice for Accelerated Aging of Asphalt Binder Using a Pressurized Aging Vessel (PAV) |
| ASTM D 6373 : 2007 : EDT 1 | Standard Specification for Performance Graded Asphalt Binder |
| ASTM D 2171 : 2007 : EDT 1 | Standard Test Method for Viscosity of Asphalts by Vacuum Capillary Viscometer |
| ASTM D 2171 : 1994 | Standard Test Method for Viscosity of Asphalts by Vacuum Capillary Viscometer |
| ASTM D 2872 : 2022 | Standard Test Method for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test) |
| ASTM D 6521 : 2004 | Standard Practice for Accelerated Aging of Asphalt Binder Using a Pressurized Aging Vessel (PAV) |
| ASTM D 6373 : 2015 | Standard Specification for Performance Graded Asphalt Binder |
| ASTM D 6521 : 2003 : REV A | Standard Practice for Accelerated Aging of Asphalt Binder Using a Pressurized Aging Vessel (PAV) |
| ASTM D 6521 : 2000 | Standard Practice for Accelerated Aging of Asphalt Binder Using a Pressurized Aging Vessel (PAV) |
| ASTM D 6373 : 2021 | Standard Specification for Performance-Graded Asphalt Binder |
| ASTM D 2872 : 1997 | Standard Test Method for Effect of Heat and Air on a Moving Film of Asphalt (Rolling Thin-Film Oven Test) |
| ASTM D 2171 : 2001 | Standard Test Method for Viscosity of Asphalts by Vacuum Capillary Viscometer |
| ASTM D 2872 : 2004 | Standard Test Method for Effect of Heat and Air on a Moving Film of Asphalt (Rolling Thin-Film Oven Test) |
| ASTM D 2171 : 2007 | Standard Test Method for Viscosity of Asphalts by Vacuum Capillary Viscometer |
| ASTM E 77 : 1998 | Standard Test Method for Inspection and Verification of Thermometers |
| ASTM D 6373 : 2007 | Standard Specification for Performance Graded Asphalt Binder |
| ASTM C 670 : 2015 | Standard Practice for Preparing Precision and Bias Statements for Test Methods for Construction Materials |
| ASTM D 2170 : 2001 | Standard Test Method for Kinematic Viscosity of Asphalts (Bitumens) |
| ASTM E 77 : 2014 : R2021 | Standard Test Method for Inspection and Verification of Thermometers |
| ASTM D 6521 : 2019 | Standard Practice for Accelerated Aging of Asphalt Binder Using a Pressurized Aging Vessel (PAV) |
Please Login or Create an Account so you can add users to your Multi user PDF Later.
Important note : All end users must be registered with an Account prior to user licenses being assigned.
Users cannot be edited or removed once added to your Multi user PDF.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.