SPECIFICATION FOR PROCESSING ADDITIONS FOR USE IN THE MANUFACTURE OF HYDRAULIC CEMENTS

Available format(s)

Hardcopy , PDF

Language(s)

English

Published date

01-01-2015

Publisher

American Association of State Highway and Transportation Officials

1. SCOPE
2. REFERENCED DOCUMENTS
3. MATERIALS
4. GENERAL REQUIREMENTS
5. SAMPLING CEMENT
6. TEST METHODS
7. TESTS ON PROCESSING ADDITIONS
8. TESTS ON CEMENT
9. CONCRETE MIXTURES
10. TESTS ON FRESHLY MIXED CONCRETE
11. TEST SPECIMENS OF HARDENED CONCRETE
12. TESTS ON HARDENED CONCRETE
13. REPORT
14. MANUFACTURERÆS CERTIFICATION PROCESSING ADDITIONS
15. KEYWORDS

Applies to the criteria and tests to be used for determining whether an organic or inorganic processing addition, when used in the recommended amount at the option of the cement producer in the manufacture of hydraulic cements, meets the requirements as prescribed by definition in M 85 and M 240 as well as ASTM C 1157/C 1157M and C 845.

DevelopmentNote	Included in AASHTO HM. (09/2013)
DocumentType	Standard
Pages	9
ProductNote	Reconfirmed 2015
PublisherName	American Association of State Highway and Transportation Officials
Status	Current
SupersededBy	AASHTO M 327:2019
Supersedes	AASHTO M 327:2011

AASHTO T 231 : 2013	PRACTICE FOR CAPPING CYLINDRICAL CONCRETE SPECIMENS
AASHTO T 152 : 2013	METHOD OF TEST FOR AIR CONTENT OF FRESHLY MIXED CONCRETE BY THE PRESSURE METHOD
ASTM C 1157/C1157M : 2017 : REDLINE	Standard Performance Specification for Hydraulic Cement
AASHTO M 85 : 2015	SPECIFICATION FOR PORTLAND CEMENT
AASHTO T 129 : 2014(R2018)	METHOD OF TEST FOR AMOUNT OF WATER REQUIRED FOR NORMAL CONSISTENCY OF HYDRAULIC CEMENT PASTE
AASHTO T 196M/T 196 : 1900	METHOD OF TEST FOR AIR CONTENT OF FRESHLY MIXED CONCRETE BY THE VOLUMETRIC METHOD
AASHTO T 107M/T 107 : 1900	METHOD OF TEST FOR AUTOCLAVE EXPANSION OF HYDRAULIC CEMENT
AASHTO M 240M/M 240 : 2016	SPECIFICATION FOR BLENDED HYDRAULIC CEMENT
AASHTO T 98M/T 98 : 2012(R2016)	METHOD OF TEST FOR FINENESS OF PORTLAND CEMENT BY THE TURBIDIMETER
AASHTO T 97 : 2014	METHOD OF TEST FOR FLEXURAL STRENGTH OF CONCRETE (USING SIMPLE BEAM WITH THIRD-POINT LOADING)
AASHTO M 80 : 2013	SPECIFICATION FOR COARSE AGGREGATE FOR HYDRAULIC CEMENT CONCRETE
AASHTO M 6 : 2013(R2018)	SPECIFICATION FOR FINE AGGREGATE FOR HYDRAULIC CEMENT CONCRETE
AASHTO T 131 : 2015	METHOD OF TEST FOR TIME OF SETTING OF HYDRAULIC CEMENT BY VICAT NEEDLE
AASHTO T 121M/T 121 : 2016	METHOD OF TEST FOR DENSITY (UNIT WEIGHT), YIELD, AND AIR CONTENT (GRAVIMETRIC) OF CONCRETE
ASTM C 226 : 2012 : REDLINE	Standard Specification for Air-Entraining Additions for Use in the Manufacture of Air-Entraining Hydraulic Cement
AASHTO T 106M/T 106 : 1900	METHOD OF TEST FOR COMPRESSIVE STRENGTH OF HYDRAULIC CEMENT MORTAR (USING 50-MM OR 2-IN. CUBE SPECIMENS)
AASHTO T 105 : 2015	METHOD OF TEST FOR CHEMICAL ANALYSIS OF HYDRAULIC CEMENT
AASHTO T 137 : 2012(R2016)	METHOD OF TEST FOR AIR CONTENT OF HYDRAULIC CEMENT MORTAR
ASTM E 203 : 2016 : REDLINE	Standard Test Method for Water Using Volumetric Karl Fischer Titration
AASHTO T 119M/T 119 : 1900	METHOD OF TEST FOR SLUMP OF HYDRAULIC CEMENT CONCRETE
AASHTO T 22 : 2014	METHOD OF TEST FOR COMPRESSIVE STRENGTH OF CYLINDRICAL CONCRETE SPECIMENS
AASHTO T 153 : 2013(R2017)	METHOD OF TEST FOR FINENESS OF HYDRAULIC CEMENT BY AIR PERMEABILITY APPARATUS