ASTM B 947 : 2014 : R2020 : EDT 1

Current
Current

The latest, up-to-date edition.

Standard Practice for Hot Rolling Mill Solution Heat Treatment for Aluminum Alloy Plate
Available format(s)

Hardcopy , PDF

Language(s)

English

Published date

01-09-2020

1.1This practice establishes the controls required for hot rolling mill solution heat treatment of the 6xxx series aluminum alloy plate in Table 1 when ASTM material specifications allow use of this process instead of furnace solution heat treatment. For the alloys listed in Table 1, this practice is an alternate process to solution heat treatment in a furnace, such as specified in Practice B918/B918M as the preliminary step for the attainment of T651-type tempers (see ANSI H35.1/H35.1M).

1.2This practice applies only to hot rolling mill solution heat treatment of plate for the listed aluminum alloys. Precipitation hardening (aging), processing, and equipment calibration for aging shall meet the practice and requirements of Practice B918/B918M.

1.3The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.

1.4This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.5This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

Committee
B 07
DocumentType
Standard Practice
Pages
4
ProductNote
ε1NOTE—Warning moved from previous Note 2 to5.3editorially in September 2020.
PublisherName
American Society for Testing and Materials
Status
Current
Supersedes

ASTM B 557 : 2015 : R2023 Standard Test Methods for Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products
ASTM B 557M : 2015 : R2023 Standard Test Methods for Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products (Metric)
ASTM B 209M : 2014 Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate (Metric) (Withdrawn 2021)
ASTM B 557M : 2002 Standard Test Methods of Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products [Metric]
ASTM B 209 : 2014 Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate
ASTM B 557 : 2015 Standard Test Methods for Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products
ASTM B 557M : 1994 Standard Test Methods of Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products [Metric]
ASTM B 557 : 1994 Standard Test Methods of Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products
ASTM B 557M : 2015 Standard Test Methods for Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products (Metric)

View more information
£45.92
Excluding VAT

Access your standards online with a subscription

Features

  • Simple online access to standards, technical information and regulations.

  • Critical updates of standards and customisable alerts and notifications.

  • Multi-user online standards collection: secure, flexible and cost effective.