Standard Guide for Resonant Ultrasound Spectroscopy for Defect Detection in Both Metallic and Non-metallic Parts
Hardcopy , PDF
English
01-11-2018
This guide describes a procedure for detecting defects in metallic and non-metallic parts using the resonant ultrasound spectroscopy method.
1.1This guide describes a procedure for detecting defects in metallic and non-metallic parts using the resonant ultrasound spectroscopy method. The procedure is intended for use with instruments capable of exciting and recording whole body resonant states within parts which exhibit acoustical or ultrasonic ringing. It is used to distinguish acceptable parts from those containing defects, such as cracks, voids, chips, density defects, tempering changes, and dimensional variations that are closely correlated with the parts' mechanical system dynamic response.
1.2The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.3This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.4This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
| Committee |
E 07
|
| DocumentType |
Guide
|
| Pages |
9
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Current
|
| Supersedes |
| ASTM E 3081 : 2016 | Standard Practice for Outlier Screening Using Process Compensated Resonance Testing via Swept Sine Input for Metallic and Non-Metallic Parts |
| ASTM E 2534 : 2015 | Standard Practice for Process Compensated Resonance Testing Via Swept Sine Input for Metallic and Non-Metallic Parts |
| ASTM C 1198 : 2009 : R2013 | Standard Test Method for Dynamic Young's Modulus, Shear Modulus, and Poisson's Ratio for Advanced Ceramics by Sonic Resonance |
| ASTM E 543 : 2015 | Standard Specification for Agencies Performing Nondestructive Testing |
| ASTM E 2985/E2985M : 2014 : R2019 | Standard Practice for Determination of Metal Purity Based on Elastic Constant Measurements Derived from Resonant Ultrasound Spectroscopy |
| ASTM E 3213 : 2019 | Standard Practice for Part-to-Itself Examination Using Process Compensated Resonance Testing Via Swept Sine Input for Metallic and Non-Metallic Parts |
| ASTM C 1259 : 2015 | Standard Test Method for Dynamic Young’s Modulus, Shear Modulus, and Poisson’s Ratio for Advanced Ceramics by Impulse Excitation of Vibration |
| ASTM E 1316 : 2022 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 1876 : 2009 | Standard Test Method for Dynamic Young's Modulus, Shear Modulus, and Poisson's Ratio by Impulse Excitation of Vibration |
| ASTM E 1876 : 2001 | Standard Test Method for Dynamic Young's Modulus, Shear Modulus, and Poisson's Ratio by Impulse Excitation of Vibration |
| ASTM E 1316 : 2011 : REV B | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2015 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 2534 : 2010 | Standard Practice for Process Compensated Resonance Testing Via Swept Sine Input for Metallic and Non-Metallic Parts |
| ASTM E 1316 : 2009 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2008 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2010 : REV C | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2020 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2017 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1876 : 2021 | Standard Test Method for Dynamic Young's Modulus, Shear Modulus, and Poisson's Ratio by Impulse Excitation of Vibration |
| ASTM E 1316 : 2013 : REV C | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2000 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2019 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2014 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2013 : REV B | Standard Terminology for Nondestructive Examinations |
| ASTM E 3081 : 2016 | Standard Practice for Outlier Screening Using Process Compensated Resonance Testing via Swept Sine Input for Metallic and Non-Metallic Parts |
| ASTM E 1316 : 2018 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1876 : 2022 | Standard Test Method for Dynamic Young's Modulus, Shear Modulus, and Poisson's Ratio by Impulse Excitation of Vibration |
| ASTM E 1316 : 2011 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2007 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2015 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2019 : REV B | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2021 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2013 : REV D | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2000 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2019 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2001 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2003 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1876 : 2007 | Standard Test Method for Dynamic Young's Modulus, Shear Modulus, and Poisson's Ratio by Impulse Excitation of Vibration |
| ASTM E 1316 : 2018 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2024 | Standard Terminology for <?Pub Dtl?>Nondestructive Examinations |
| ASTM E 1316 : 2006 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 1876 : 2015 | Standard Test Method for Dynamic Young's Modulus, Shear Modulus, and Poisson's Ratio by Impulse Excitation of Vibration |
| ASTM E 1316 : 2016 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2021 : REV D | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2002 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 3081 : 2021 | Standard Practice for Outlier Screening Using Process Compensated Resonance Testing via Swept Sine Input for Metallic and Non-Metallic Parts |
| ASTM E 1316 : 2014 : EDT 1 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2010 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 1876 : 2000 | Standard Test Method for Dynamic Young's Modulus, Shear Modulus, and Poisson's Ratio by Impulse Excitation of Vibration |
| ASTM E 1316 : 2022 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2013 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2021 : REV B | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2017 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2016 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2009 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2002 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2004 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2007 : REV C | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2010 : REV B | Standard Terminology for Nondestructive Examinations |
| ASTM E 2534 : 2015 | Standard Practice for Process Compensated Resonance Testing Via Swept Sine Input for Metallic and Non-Metallic Parts |
| ASTM E 1316 : 2013 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 1876 : 1999 | Standard Test Method for Dynamic Young's Modulus, Shear Modulus, and Poisson's Ratio by Impulse Excitation of Vibration |
| ASTM E 1316 : 2023 : REV A | Standard Terminology for Nondestructive Examinations |
| ASTM E 1876 : 2001 : R2006 | Standard Test Method for Dynamic Young's Modulus, Shear Modulus, and Poisson's Ratio by Impulse Excitation of Vibration |
| ASTM E 1316 : 2021 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2007 : REV B | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2005 | Standard Terminology for Nondestructive Testing |
| ASTM E 1316 : 2004 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2021 : REV C | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2007 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2023 | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2023 : REV B | Standard Terminology for Nondestructive Examinations |
| ASTM E 1316 : 2012 | Standard Terminology for Nondestructive Examinations |
Please Login or Create an Account so you can add users to your Multi user PDF Later.
Important note : All end users must be registered with an Account prior to user licenses being assigned.
Users cannot be edited or removed once added to your Multi user PDF.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.