Specification for tube of aluminium-copper-magnesium-silicon-manganese alloy (solution treated and aged at room temperature) (not exceeding 10 mm wall thickness) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8)

Available format(s)

Hardcopy , PDF

Language(s)

English

Published date

31-08-1971

Publisher

British Standards Institution

Describes manufacture, inspection and testing of heat resisting alloys for aerospace purposes. Gives chemical composition and mechanical properties. This covers Tube of aluminium copper magnesium silicon manganese alloy.

Committee	ACE/61/-/24
DevelopmentNote	Supersedes 69/23023 DC and BS 2L62(1961). (07/2005) Reviewed and confirmed by BSI, January 2011. (12/2010)
DocumentType	Standard
Pages	8
PublisherName	British Standards Institution
Status	Current
Supersedes	BS 2L 62:1961 BS 2L62(1961) : LATEST

BS 3L 63:1971	Specification for tube of aluminium-copper-mangesium-silicon-manganese alloy (solution treated and precipitation treated) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8)
DEFSTAN 81-24/4(2002) : 2002	IDENTIFICATION MARKING OF TRANSPORTABLE CONTAINERS, COMPRESSED GAS
DEFSTAN 81-24/5(2004) : 2004	IDENTIFICATION MARKING OF TRANSPORTABLE CONTAINERS, COMPRESSED GAS
BS 2L 77:1971	Specification for forging stock and forgings of aluminium-copper-magnesium-silicon-manganese alloy (solution treated and precipitation treated) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8)
BS L 103:1971	Specification for forging stock and forgings of aluminium-copper-magnesium-silicon-manganese alloy (solution treated and aged at room temperature) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8)
BS L 102:1971	Specification for bars and extruded sections of aluminium-copper-magnesium-silicon-manganese alloy (solution treated and aged at room temperature) (not exceeding 200 mm diameter or minor sectional dimension) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8)
BS 2L 87:1971	Specification for hexagonal bars for nuts, couplings and hollow machined parts of aluminium-copper-magnesium-silicon-manganese alloy (solution treated and precipitation treated) (free from peripheral and asymmetric coarse grain) (not less than 14 mm nor more than 36 mm across flats) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8)
BS 2L 93:1971	Specification for plate of aluminium-copper-magnesium-silicon-manganese alloy (solution treated, controlled stretched and precipitation treated) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8)

BS L108(1971) : LATEST
BS 4L 100:1993	Procedure for inspection, testing and acceptance of wrought aluminium and aluminium alloys
BS 3763:1964	The International System of units (SI)
BS L104(1971) : LATEST
BS 6L 37:1971	Specification for wire for solid, cold-forged rivets of aluminium-copper-magnesium-silicon-manganese alloy (not exceeding 10 mm diameter) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8)
BS 3L 63:1971	Specification for tube of aluminium-copper-mangesium-silicon-manganese alloy (solution treated and precipitation treated) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8)
BS L 103:1971	Specification for forging stock and forgings of aluminium-copper-magnesium-silicon-manganese alloy (solution treated and aged at room temperature) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8)
BS L107(1971) : LATEST
BS L106(1971) : LATEST
BS 350:2004	Conversion factors for units