EN 2489 : 1995
Current
Current
The latest, up-to-date edition.
AEROSPACE SERIES - FIBRE REINFORCED PLASTICS - DETERMINATION OF THE ACTION OF TEST FLUIDS
Published date
20-09-1995
Publisher
Foreword
1 Scope
2 Normative references
3 Principle
4 Test fluids
5 Apparatus
6 Specimens
7 Procedure
8 Expression of results
9 Designation
10 Test report
This standard specifies the method of immersion of fibre reinforced plastics in test fluids.
DevelopmentNote |
Supersedes PREN 2489. (11/2003)
|
DocumentType |
Standard
|
PublisherName |
Comite Europeen de Normalisation
|
Status |
Current
|
Supersedes |
Standards | Relationship |
DIN EN 2489:1995-11 | Identical |
UNI EN 2489 : 1995 | Identical |
SNV DIN EN 2489 : 1995 | Identical |
PN EN 2489 : 1999 | Identical |
BS EN 2489:1995 | Identical |
NBN EN 2746 : 1998 | Identical |
NBN EN 2489 : 1996 | Identical |
NS EN 2489 : 1ED 1995 | Identical |
I.S. EN 2489:1996 | Identical |
UNE-EN 2489:1996 | Identical |
NEN EN 2489 : 1995 | Identical |
NF EN 2489 : 1996 | Identical |
93/706616 DC : 0 | PREN 2833-1 - AEROSPACE SERIES - TECHNICAL SPECIFICATION - GLASS FIBER THERMOSETTING PREIMPREGNATES - PART 1: GENERAL |
PREN 2833-3 : 200P1 | AEROSPACE SERIES - GLASS FIBRE THERMOSETTING PREIMPREGNATES - TECHNICAL SPECIFICATION - PART 3: GLASS FABRIC/EPOXY RESIN PREIMPREGNATE CURING AT UP 180 DEGREES C FOR CONTINUOUS USE UP TO 120 DEGREES C |
I.S. EN 6035:2015 | AEROSPACE SERIES - FIBRE REINFORCED PLASTICS - TEST METHOD - DETERMINATION OF NOTCHED AND UNNOTCHED TENSILE STRENGTH |
SAE AMS 2980/1 : 2014 | CARBON FIBER FABRIC AND EPOXY RESIN WET LAY-UP REPAIR MATERIAL - PART 1 - GENERAL REQUIREMENTS |
I.S. EN 6036:2015 | AEROSPACE SERIES - FIBRE REINFORCED PLASTICS - TEST METHOD - DETERMINATION OF NOTCHED, UNNOTCHED AND FILLED HOLE COMPRESSION STRENGTH |
I.S. EN 2833-005:2013 | AEROSPACE SERIES - GLASS FIBRE THERMOSETTING PREIMPREGNATES - TECHNICAL SPECIFICATION - PART 005: GLASS FABRIC/PHENOLIC RESIN PREIMPREGNATE |
EN 2850:2017 | Aerospace series - Carbon fibre thermosetting resin - Unidirectional laminates - Compression test parallel to fibre direction |
DIN EN 2561:1995-11 | AEROSPACE SERIES - CARBON FIBRE REINFORCED PLASTICS - UNIDIRECTIONAL LAMINATES - TENSILE TEST PARALLEL TO THE FIBRE DIRECTION |
DIN EN 2746:1998-10 | AEROSPACE SERIES - GLASS FIBRE REINFORCED PLASTICS - FLEXURAL TEST, THREE POINT BEND METHOD |
BS EN 2597:1998 | Carbon fibre reinforced plastics. Unidirectional laminates. Tensile test perpendicular to the fibre direction |
BS EN 2850:2017 | Aerospace series. Carbon fibre thermosetting resin - Unidirectional laminates. Compression test parallel to fibre direction |
BS EN 6035:2015 | Aerospace series. Fibre reinforced plastics. Test method. Determination of notched and unnotched tensile strength |
UNI EN 2833-005 : 2014 | AEROSPACE SERIES - GLASS FIBRE THERMOSETTING PREIMPREGNATES - TECHNICAL SPECIFICATION - PART 005: GLASS FABRIC/PHENOLIC RESIN PREIMPREGNATE |
PREN 2833-5 : 200P1 | AEROSPACE SERIES - GLASS FIBRE THERMOSETTING PREIMPREGNATES - TECHNICAL SPECIFICATION - PART 5: GLASS FABRIC/PHENOLIC RESIN PREIMPREGNATE |
DIN EN 2562:1997-05 | AEROSPACE SERIES - CARBON FIBRE REINFORCED PLASTICS - UNIDIRECTIONAL LAMINATES - FLEXURAL TEST PARALLEL TO THE FIBRE DIRECTION |
DIN EN 2597:1998-08 | AEROSPACE SERIES - CARBON FIBRE REINFORCED PLASTICS - UNIDIRECTIONAL LAMINATES - TENSILE TEST PERPENDICULAR TO THE FIBRE DIRECTION |
EN 6035:2015 | Aerospace series - Fibre reinforced plastics - Test method - Determination of notched and unnotched tensile strength |
EN 2562 : 1997 | AEROSPACE SERIES - CARBON FIBRE REINFORCED PLASTICS - UNIDIRECTIONAL LAMINATES - FLEXURAL TEST PARALLEL TO THE FIBRE DETECTION |
95/714421 DC : 0 | PREN 2833-3 - AEROSPACE SERIES - GLASS FIBRE THERMOSETTING PREIMPREGNATES - TECHNICAL SPECIFICATION - PART 3: GLASS FABRIC/EPOXY RESIN PREIMPREGNATE CURING AT UP TO 180 DEGREE C FOR CONTINUOUS USE UP TO 120 DEGREE C |
SAE AMS 3970/6 : 2011 | CARBON FIBER FABRIC REPAIR PREPREG, 120 DEGREES C (250 DEGREES F) VACUUM CURING - PART 6 - MATERIAL SPECIFICATION: CARBON FIBER FABRIC REINFORCED EPOXY PREPREG FOR REPAIR, PLAIN WEAVE FABRIC, 193 G/M[2], ADHESIVE FILM FOR REPAIR AND NON-STRUCTURAL GLASS FIBER FABRIC REINFORCED EPOXY PREPREG, 105 G/M[2] |
BS EN 6036:2015 | Aerospace series. Fibre reinforced plastics. Test method. Determination of notched, unnotched and filled hole compression strength |
BS EN 6031:2015 | Aerospace series. Fibre reinforced plastics. Test method. Determination of in-plane shear properties (± 45° tensile test) |
BS EN 2563:1997 | Carbon fibre reinforced plastics. Unidirectional laminates. Determination of the apparent interlaminar shear strength |
BS EN 2747:1998 | Glass fibre reinforced plastics. Tensile test |
BS EN 2561:1995 | Carbon fibre reinforced plastics. Undirectional laminates. Tensile test parallel to the fibre direction |
BS EN 2746:1998 | Glass fibre reinforced plastics. Flexural test. Three point bend method |
EN 2597 : 1998 | AEROSPACE SERIES - CARBON FIBRE REINFORCED PLASTICS - UNIDIRECTIONAL LAMINATES - TENSILE TEST PERPENDICULAR TO THE FIBRE DIRECTION |
EN 2747:1998 | Aerospace series - Glass fibre reinforced plastics - Tensile test |
EN 2561 : 1995 | AEROSPACE SERIES - CARBON FIBRE REINFORCED PLASTICS - UNIDIRECTIONAL LAMINATES - TENSILE TEST PARALLEL TO THE FIBRE DIRECTION |
EN 2746:1998 | Aerospace series - Glass fibre reinforced plastics - Flexural test - Three point bend method |
EN 2563 : 1997 | AEROSPACE SERIES - CARBON FIBRE REINFORCED PLASTICS - UNIDIRECTIONAL LAMINATES - DETERMINATION OF THE APPARENT INTERLAMINAR SHEAR STRENGTH |
EN 6031:2015 | Aerospace series - Fibre reinforced plastics - Test method - Determination of in-plane shear properties (± 45° tensile test) |
EN 2833-005:2013 | Aerospace series - Glass fibre thermosetting preimpregnates - Technical specification - Part 005: Glass fabric/phenolic resin preimpregnate |
EN 6036:2015 | Aerospace series - Fibre reinforced plastics - Test method - Determination of notched, unnotched and filled hole compression strength |
I.S. EN 6031:2015 | AEROSPACE SERIES - FIBRE REINFORCED PLASTICS - TEST METHOD - DETERMINATION OF IN-PLANE SHEAR PROPERTIES (+/- 45 DEGREES TENSILE TEST) |
SAE AMS 3970/1 : 2011 | CARBON FIBER FABRIC REPAIR PREPREG, 120 DEGREES C (250 DEGREES F) VACUUM CURING - PART 1 - GENERAL REQUIREMENTS |
DIN EN 6061:1996-04 (Draft) | AEROSPACE SERIES - FIBRE REINFORCED PLASTICS - TEST METHOD - DETERMINATION OF SANDWICH FLEXURAL STRENGTH, 4 POINT BENDING |
93/711194 DC : 0 | PREN 2833-2 - TECHNICAL SPECIFICATION - GLASS FIBRE THERMOSETTING PREIMPREGNATES - PART 2: GLASS FABRIC/EPOXY RESIN PREIMPREGNATES CURING AT 125 DEGREES C FOR CONTINUOUS USE UP TO 80 DEGREES C |
BS EN 2833-005:2013 | Aerospace series. Glass fibre thermosetting preimpregnates. Technical specification Glass fabric/phenolic resin preimpregnate |
95/714422 DC : 0 | PREN 2833-4 - AEROSPACE SERIES - GLASS FIBER THERMOSETTING PREIMPREGNATES - TECHNICAL SPECIFICATION - PART 4: UNIDIRECTIONAL GLASS/EPOXY RESIN PREIMPREGNATE CURING AT UP TO 125 DEGREE C FOR CONTINUOUS USE UP TO 80 DEGREE C |
PREN 2833-4 : 200P1 | AEROSPACE SERIES - GLASS FIBRE THERMOSETTING PREIMPREGNATES - TECHNICAL SPECIFICATION - PART 4: UNIDIRECTIONAL GLASS/EPOXY RESIN PREIMPREGNATE CURING AT UP TO 125 DEGREES C FOR CONTINUOUS USE UP TO 80 DEGREES C |
I.S. EN 2850:2017 | AEROSPACE SERIES - CARBON FIBRE THERMOSETTING RESIN - UNIDIRECTIONAL LAMINATES - COMPRESSION TEST PARALLEL TO FIBRE DIRECTION |
PREN 2379 : 200P1 | AEROSPACE SERIES - FLUIDS FOR ASSESSMENT OF NON-METALLIC MATERIALS |
PREN 2743 : 200P1 | AEROSPACE SERIES - REINFORCED PLASTICS - STANDARD PROCEDURES FOR CONDITIONING PRIOR TO TESTING |
EN 2744:1992 | Aerospace series - Non metallic materials - Preferred test temperatures |
Sorry this product is not available in your region.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.