Describes corrosion inhibiting, chemical and solvent resistant, solvent-borne, high-solids epoxy primer coatings that have a maximum volatile organic compound (VOC) content of 340 grams per liter (g/L)(2.8 pounds per gallon [lb/gal]).
Committee |
FSC 8010
|
DevelopmentNote |
Supersedes MIL P 23377 (F). (07/2004)
|
DocumentType |
Standard
|
Pages |
20
|
ProductNote |
NEW CHILD NOT 1 2019 IS NOW ADDED.
|
PublisherName |
US Military Specs/Standards/Handbooks
|
Status |
Current
|
Supersedes |
MIL-PRF-32239 Revision A:2014 | COATING SYSTEM, ADVANCED PERFORMANCE, FOR AEROSPACE APPLICATIONS |
MIL-PRF-32104 Base Document:2010 | MOBILE HYDRAULIC OIL DISPENSER |
MIL-DTL-53072 Revision F:2017 | CHEMICAL AGENT RESISTANT COATING (CARC) SYSTEM - APPLICATION PROCEDURES AND QUALITY CONTROL INSPECTION |
SAE AMS 2477 : 2010 | CONVERSION COATING FOR ALUMINUM ALLOYS LOW ELECTRICAL RESISTANCE COATING |
MIL-PRF-32405 Base Document:2013 | CLEANER, HAND WIPE, FOR AVIATION AND MISSILE SYSTEMS, METALLIC SUBSTRATES, LOW OR EXEMPT VOC |
SAE AMS 3166 : 2014 | SOLVENTS, CLEANING, CLEANING PRIOR TO APPLICATION OF SEALING COMPOUNDS |
SAE AIR 5479 : 2017 | ENVIRONMENTALLY COMPLIANT PROCESSES FOR LANDING GEAR |
MIL-PRF-22750 Revision G:2011 | COATING, EPOXY, HIGH-SOLIDS |
MIL-PRF-85322 Revision C:2014 | COATING, ELASTOMERIC, POLYURETHANE, RAIN-EROSION |
MIL-PRF-81309 Revision G:2014 | CORROSION PREVENTIVE COMPOUNDS, WATER DISPLACING, ULTRA-THIN FILM |
MIL-PRF-6799 Revision L:2010 | COATINGS, SPRAYABLE, STRIPPABLE, PROTECTIVE, WATER EMULSION |
SAE AS 6116 : 2016 | ALUMINUM FITTINGS, AXIALLY SWAGED TUBE WITH FLARELESS SEPERABLE, FLUID SYSTEM, UP TO 1500 PSI (10340 KPA) MAXIMUM, SPECIFICATION FOR |
SAE AMS 3278 : 2016 | SEALING AND COATING COMPOUND, POLYURETHANE (PUR), FUEL RESISTANT, HIGH TENSILE STRENGTH/ELONGATION, FOR INTEGRAL FUEL TANKS/FUEL CAVITIES/GENERAL PURPOSE |
SAE AMS 3167 : 2005 | SOLVENTS, WIPE FOR CLEANING PRIOR TO APPLICATION OF PRIMER AND TOP COAT MATERIALS, OR SEALING COMPOUNDS |
SAE AMS 2480 : 2013 | PHOSPHATE TREATMENT PAINT BASE |
SAE AMS 3255 : 2017 | SEALING TAPE, SHEET, OR GASKET, POLYTETRAFLUOROETHYLENE, EXPANDED (EPTFE) OIL AND WATER RESISTANT |
SAE AMS 3379 : 2013(R2018) | SEALING COMPOUND, POLYSULFIDE RUBBER PREFORMED STRIPS FOR SEALING REMOVABLE DOORS, SKINS, AND PANELS |
ASTM F 502 : 2008 | Standard Test Method for Effects of Cleaning and Chemical Maintenance Materials on Painted Aircraft Surfaces |
MIL-DTL-14072 Revision F:2013 | FINISHES FOR GROUND BASED ELECTRONIC EQUIPMENT |
MIL-STD-769 Revision K:2015 | Insulation Requirements for U.S. Naval Vessels |
MIL STD 11991 : A | GENERAL STANDARD FOR PARTS, MATERIALS, AND PROCESSES |
MIL-DTL-55041 Revision F:2012 | Switches, Waveguide, General Specification for |
MIL-DTL-62478 Revision C:2010 | COUPLER, OPTICAL |
P-W-2891 Revision A:2002 | WIPE SOLVENTS, EXEMPT AND NON-EXEMPT |
SAE AMS 3265 : 2015 | SEALING COMPOUND, POLYSULFIDE (T) RUBBER, FUEL RESISTANT, NON-CHROMATED CORROSION INHIBITING, FOR INTERMITTENT USE TO 360 DEGREES F (182 DEGREES C) |
MIL-PRF-85570 Revision E:2012 | CLEANING COMPOUNDS, AIRCRAFT, EXTERIOR |
SAE AMS 3276 : 2016 | SEALING COMPOUND, INTEGRAL FUEL TANKS AND GENERAL PURPOSE, INTERMITTENT USE TO 360 DEGREES F (182 DEGREES C) |
SAE AMS 3102 : 2017 | SEALING COMPOUND, POLYTHIOETHER RUBBER FAST CURING, LIGHT WEIGHT (SPECIFIC GRAVITY 0.78, MAX.) FOR INTEGRAL FUEL TANKS AND GENERAL PURPOSE, INTERMITTENT USE TO 360 DEGREES F (182 DEGREES C) |
SAE AS 5127 : 2013 | AEROSPACE STANDARD TEST METHODS FOR AEROSPACE SEALANTS METHODS FOR PREPARING AEROSPACE SEALANT TEST SPECIMENS |
ASTM F 502 : 2008 : R2013 | Standard Test Method for Effects of Cleaning and Chemical Maintenance Materials on Painted Aircraft Surfaces |
MIL-PRF-81352 Revision C:2005 | COATINGS, AIRCRAFT TOUCH-UP |
SAE AS 5958 : 2017 | FITTINGS, AXIALLY SWAGED TUBE WITH FLARELESS SEPARABLE, FLUID SYSTEM FOR OPERATING PRESSURES UP TO AND INCLUDING 5080 PSI (35 000 KPA), SPECIFICATION FOR |
SAE AMS 3100 : 2013 | ADHESION PROMOTER FOR POLYSULFIDE SEALING COMPOUNDS |
MIL-PRF-81975 Revision C:2008 | COUPLINGS, REGULATED, AERIAL PRESSURE REFUELING TYPE MA-2, TYPE MA-3 AND TYPE MA-4 |
MIL-PRF-7907 Revision C:2007 | Cleaning Compound, Decontaminating (for Soiled and Radioactive Contaminated Surfaces) |
MIL-PRF-32479 Revision A:2017 | TRAILERS, LIFT - AIRCRAFT AND MISSILE ENGINE |
MIL-PRF-26139 Revision E:2015 | TESTER, PRESSURIZED CABIN LEAKAGE, AIRCRAFT, (AF/M24T-3 AND AF/M32T-1) |
SAE MA 2114 : 2017 | ADAPTER - PORT CONNECTION, RING LOCKED INSTALLATION AND REMOVAL OF |
MIL-PRF-85285 Revision E:2012 | COATING: POLYURETHANE, AIRCRAFT AND SUPPORT EQUIPMENT |
MIL-DTL-32459 Base Document:2013 | Coatings, Anodic for Magnesium and Magnesium Alloys |
MIL-PRF-32090 Revision A:2016 | DELIVERY SYSTEM, AERIAL, BULK FUEL |
MIL-DTL-18264 Revision E:2015 | FINISHES, ORGANIC, WEAPONS SYSTEMS, APPLICATION AND CONTROL OF |
SAE AMS 3277 : 2015 | SEALING COMPOUND, POLYTHIOETHER RUBBER, FAST CURING FOR INTEGRAL FUEL TANKS AND GENERAL PURPOSE, INTERMITTENT USE TO 360 DEGREES F (182 DEGREES C) |
SAE AS 5551 : 2017 | FITTING ASSEMBLY - 24 DEGREES CONE FLARELESS PER AS5827, 5080 PSI, PORT CONNECTION, PORT PREPARATION, INSTALLATION AND REMOVAL OF AS5550 AND AS5865 |
NASA STD 5020 : 2012 | REQUIREMENTS FOR THREADED FASTENING SYSTEMS IN SPACEFLIGHT HARDWARE |
NASA MSFC HDBK 3697 : 2014 | ELECTRICAL BONDING DESIGN GUIDE HANDBOOK |
MIL-STD-186 Revision F:2002 | PROTECTIVE FINISHING SYSTEMS FOR ROCKETS, GUIDED MISSILES, SUPPORT EQUIPMENT AND RELATED MATERIALS |
MIL-STD-3035 Base Document:2013 | DESIGN CRITERIA STANDARD - USAF AIRCRAFT ARRESTING SYSTEMS |
MIL-PRF-32390 Base Document:2011 | ENGAGING DEVICE, AIRCRAFT ARRESTING SYSTEM - USAF PENDANT CABLE RETRACTION SYSTEMS (PCRS) |
SAE AS 1301 : 2015 | ADAPTERS - PORT CONNECTION, RING LOCKED DESIGN, INSTALLATION AND REMOVAL OF |
MIL-DTL-5541 Revision F:2006 | Chemical Conversion Coatings on Aluminum and Aluminum Alloys |
MIL-STD-7179 Revision A:2009 | Finishes, Coatings, and Sealants, for the Protection of Aerospace Weapons Systems and Support Equipment |
MIL-PRF-83323 Revision D:2016 | TESTER, UNIVERSAL RECEPTACLE, AERIAL REFUELING |
MIL-DTL-32392 Revision A:2013 | AIRCRAFT ARRESTING SYSTEM - TEXTILE (TAAS) |
MIL-STD-171 Revision F:2011 | FINISHING OF METAL AND WOOD SURFACES |
SAE AMS 3281 : 2016 | SEALING COMPOUND, POLYSULFIDE (T) SYNTHETIC RUBBER FOR INTEGRAL FUEL TANK AND FUEL CELL CAVITIES LOW DENSITY FOR INTERMITTENT USE TO 360 DEGREES F (182 DEGREES C) |
MIL-STD-2161 Revision C:2014 | Paint Schemes and Exterior Markings for U.S. Navy and Marine Corps Aircraft |
MIL-DTL-64159 Revision B:2011 | CAMOUFLAGE COATING, WATER DISPERSIBLE ALIPHATIC POLYURETHANE, CHEMICAL AGENT RESISTANT |
SAE AMS 2486 : 2010 | CONVERSION COATING OF TITANIUM ALLOYS FLUORIDE-PHOSPHATE TYPE |
NASM25027:2012 | NUT, SELF-LOCKING, 250 DEGREES F, 450 DEGREES F, AND 800 DEGREES F |
SAE AS 5127/1 : 2014 | AEROSPACE STANDARD TEST METHODS FOR AEROSPACE SEALANTS TWO-COMPONENT SYNTHETIC RUBBER COMPOUNDS |
SAE AMS 3603 : 2002 | PROTECTIVE FILM, HIGH PERFORMANCE, POLYMERIC PRESSURE SENSITIVE ADHESIVE, FOR AIRCRAFT EXTERIOR APPLICATIONS |
MIL-PRF-81733 Revision D:1998 | SEALING AND COATING COMPOUND, CORROSION INHIBITIVE |
MIL-DTL-55288 Revision E:2012 | Antenna AS-1729/VRC |
MIL-DTL-81706 Revision B:2004 | Chemical Conversion Materials for Coating Aluminum and Aluminum Alloys |
SAE AMS S 8802 : 2015 | SEALING COMPOUND, FUEL RESISTANT, INTEGRAL FUEL TANKS AND FUEL CELL CAVITIES |
SAE AMS 2473 : 2013 | CHEMICAL FILM TREATMENT FOR ALUMINUM ALLOYS, GENERAL PURPOSE COATING |
MIL-DTL-53039 Revision E:2013 | COATING, ALIPHATIC POLYURETHANE, SINGLE COMPONENT, CHEMICAL AGENT RESISTANT |
MIL-PRF-32587 Base Document:2018 | Remover, Paint, Hap-Free, Neutral |
MIL-PRF-32470 Base Document:2013 | TRUCK, FORKLIFT, 10,000 LB CAPACITY, VARIABLE REACH, ROUGH TERRAIN |
MIL-PRF-87937 Revision D:2001 | CLEANING COMPOUND, AEROSPACE EQUIPMENT |
SAE AMS 3284 : 2017 | SEALING COMPOUND, LOW ADHESION, FOR REMOVABLE PANELS AND FUEL TANK INSPECTION PLATES |
SAE AMS 3144 : 2012 | PRIMER, ANODIC ELECTRODEPOSITION FOR AIRCRAFT APPLICATIONS |
MIL-STD-1568 Revision D:2015 | Materials and Processes for Corrosion Prevention and Control in Aerospace Weapons Systems |
SAE ARP 4118 : 2013 | ISOLATION AND CORROSION PROTECTION OF DISSIMILAR MATERIALS, CARBON COMPOSITE STRUCTURE REPAIR |
SAE AMS 3092 : 2015 | RELEASE AGENT, FOR USE DURING FORM-IN-PLACE GASKET PREPARATION |
SAE AMS 1640 : 2011 | CORROSION REMOVING COMPOUND, FOR AIRCRAFT SURFACES |
ASTM D 823 : 1995 | Standard Practices for Producing Films of Uniform Thickness of Paint, Varnish, and Related Products on Test Panels |
ASTM D 5895 : 2013 : REDLINE | Standard Test Methods for Evaluating Drying or Curing During Film Formation of Organic Coatings Using Mechanical Recorders |
MIL-PRF-85285 Revision E:2012 | COATING: POLYURETHANE, AIRCRAFT AND SUPPORT EQUIPMENT |
SAE AMS QQ A 250/4 : 2015 | ALUMINUM ALLOY 2024, PLATE AND SHEET |
ASTM D 1200 : 2010 | Standard Test Method for Viscosity by Ford Viscosity Cup |
MIL-DTL-5541 Revision F:2006 | Chemical Conversion Coatings on Aluminum and Aluminum Alloys |
TT-R-2918 Revision A:2001 | REMOVAL, PAINT, NO HAZARDOUS AIR POLLUTANTS (HAPS) |
MIL-C-8514 Revision C:1967 | COATING, COMPOUND, METAL PRETREATMENT, RESIGN ACID [ASG] |
MIL-R-81294 Revision D:1990 | REMOVER, PAINT, EPOXY, POLYSULPHIDE AND POLYURETHANE SYSTEMS |
MIL-PRF-23699 Revision G:2014 | Lubricating Oil, Aircraft Turbine Engine, Synthetic Base, NATO Code Numbers: O-152, O-154, O-156, and O-167 |
SAE AMS QQ A 250/5 : 2014 | ALUMINUM ALLOY ALCLAD 2024, PLATE AND SHEET |
MIL A 8625 : F | ANODIC COATINGS FOR ALUMINUM AND ALUMINUM ALLOYS |
MIL T 81772 : B | THINNER, AIRCRAFT COATING |
MIL-PRF-83282 Revision D:1997 | HYDRAULIC FLUID, FIRE RESISTANT, SYNTHETIC HYDROCARBON BASE, METRIC, NATO CODE NUMBER H-537 |
FED-STD-595 Revision C:2008 | COLORS USED IN GOVERNMENT PROCUREMENT |
ASTM D 3359 : 2017 : REDLINE | Standard Test Methods for Rating Adhesion by Tape Test |
Please Login or Create an Account so you can add users to your Multi user PDF Later.
Important note : All end users must be registered with an Account prior to user licenses being assigned.
Users cannot be edited or removed once added to your Multi user PDF.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.