SAE AMS 2664 : 2014

Superseded

View Superseded by

BRAZING, SILVER, FOR USE UP TO 800 DEGREES F (427 DEGREES C)

Available format(s)

Hardcopy , PDF

Superseded date

11-07-2019

Language(s)

English

Published date

01-01-2014

Publisher

SAE International

1. SCOPE
2. APPLICABLE DOCUMENTS
3. TECHNICAL REQUIREMENTS
4. QUALITY ASSURANCE PROVISIONS
5. PREPARATION FOR DELIVERY
6. ACKNOWLEDGMENT
7. REJECTIONS
8. NOTES

Specifies the engineering requirements for producing brazed joints in parts made of steels, iron alloys, nickel alloys, and cobalt alloys by use of silver alloy filler metals, and the properties of such joints.

Committee	AMS-B
DevelopmentNote	Supersedes SAE AMS 2666 (07/1999)
DocumentType	Standard
Pages	9
PublisherName	SAE International
Status	Superseded
SupersededBy	SAE AMS 2664F : 1995(R2019)
Supersedes	SAE AMS 2664 : 1995 SAE AMS 2666 : 1995

SAE AMS 2424 : 2010	PLATING, NICKEL LOW-STRESSED DEPOSIT
MIL-STD-2073-1 Revision E:2008	STANDARD PRACTICE FOR MILITARY PACKAGING
SAE AMS 4765 : 2015	SILVER ALLOY, BRAZING FILLER METAL 56AG - 42CU - 2.0NI 1420 TO 1640 DEGREES F (771 TO 893 DEGREES C) SOLIDUS-LIQUIDUS RANGE
SAE AMS 4772 : 2015	SILVER ALLOY, BRAZING FILLER METAL, 54AG - 40CU - 5.0ZN - 1.0NI, 1325 TO 1575 DEGREES F (718 TO 857 DEGREES C) SOLIDUS-LIQUIDUS RANGE
SAE AMS 2403 : 2015	PLATING, NICKEL, GENERAL PURPOSE
SAE AMS 3411 : 2016	FLUX, SILVER BRAZING HIGH TEMPERATURE
SAE AMS 4774 : 2015	SILVER ALLOY BRAZING FILLER METAL 63AG - 28.5CU - 6.0SN - 2.5NI 1275 TO 1475 DEGREES F (691 TO 802 DEGREES C) SOLIDUS-LIQUIDUS RANGE
SAE AMS 3417 : 2002	FLUX, BRAZING, HIGH TEMPERATURE
ASTM D 1179 : 2016 : REDLINE	Standard Test Methods for Fluoride Ion in Water