SAE AS 7251 : 2014

Superseded

View Superseded by

NUTS, SELF-LOCKING, STEEL, CORROSION AND HEAT RESISTANT HIGH STRENGTH, ALL METAL 1200 DEGREES F USE, UNJ THREAD FORM

Available format(s)

Hardcopy , PDF

Superseded date

02-03-2020

Language(s)

English

Published date

01-01-2014

Publisher

SAE International

1. SCOPE
2. REFERENCES
3. TECHNICAL REQUIREMENTS
4. QUALITY ASSURANCE PROVISIONS
5. PREPARATION FOR DELIVERY
6. ACKNOWLEDGMENT
7. REJECTIONS
8. NOTES

Specifies all metal, self-locking wrenching nuts, plate nuts, shank nuts, and gang channel nuts made from a corrosion and heat resistant steel of the type identified under the Unified Numbering System as UNS S66286 and of 160 ksi tensile strength at room temperature, with maximum test temperature of parts at 1200 degrees F.

Committee	E-25
DevelopmentNote	Supersedes SAE AMS 7251 (07/1999)
DocumentType	Revision
Pages	24
PublisherName	SAE International
Status	Superseded
SupersededBy	SAE AS7251C:2014(R2020)
Supersedes	SAE AS 7251 : 2001 SAE AMS 7251 : D1991

SAE AMS 5737 : 2012	STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS AND TUBING, 15CR - 25.5NI - 1.2MO - 2.1TI - 0.006B - 0.30V, CONSUMABLE ELECTRODE MELTED, 1650 DEGREES F (899 DEGREES C), SOLUTION AND PRECIPITATION HEAT TREATED
SAE AS 7482 : 2015	STUDS, CORROSION AND HEAT RESISTANT STEEL, UNS S66286, TENSILE STRENGTH 130 KSI, 1800 DEGREES F SOLUTION HEAT TREATED, AGED BEFORE ROLL THREADING PROCUREMENT SPECIFICATION
MIL-PRF-7808 Revision L:1997	LUBRICATING OIL, AIRCRAFT TURBINE ENGINE, SYNTHETIC BASE
SAE AMS 5853 : 2012	STEEL, CORROSION AND HEAT-RESISTANT, BARS AND WIRE, 15CR - 25.5NI - 1.2MO - 2.1TI - 0.006B - 0.30V, CONSUMABLE ELECTRODE MELTED 1800 DEGREES F (982 DEGREES C) SOLUTION TREATED AND WORK-STRENGTHENED, 160 KSI (1103 MPA) TENSILE STRENGTH
ASME B46.1 : 2009	SURFACE TEXTURE (SURFACE ROUGHNESS, WAVINESS, AND LAY)
SAE AMS 5734 : 2012	STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS, AND TUBING, 15CR - 25.5NI - 1.2MO - 2.1TI - 0.006B - 0.30V, CONSUMABLE ELECTRODE MELTED, 1650 DEGREES F (899 DEGREES C) SOLUTION HEAT TREATED
SAE AS 3071 : 2012	ACCEPTANCE CRITERIA - MAGNETIC PARTICLE, FLUORESCENT PENETRANT, AND CONTRAST DYE PENETRANT INSPECTION
SAE AS 954 : 2011	WRENCHES, HAND, TWELVE POINT, HIGH STRENGTH, THIN WALL
SAE AMS 5732 : 2012	STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS, TUBING AND RINGS, 15CR - 25.5NI - 1.2MO - 2.1TI - 0.006B - 0.30V, CONSUMABLE ELECTRODE MELTED 1800 DEGREES F (982 DEGREES C), SOLUTION AND PRECIPITATION HEAT TREATED
NASM1312-6:2013	FASTENER TEST METHODS, METHOD 6, HARDNESS
ASTM E 1417/E1417M : 2016 : REDLINE	Standard Practice for Liquid Penetrant Testing
SAE AS 8879 : 2004	SCREW THREADS - UNJ PROFILE, INCH CONTROLLED RADIUS ROOT WITH INCREASED MINOR DIAMETER
ASME Y14.36M : 1996	SURFACE TEXTURE SYMBOLS
SAE AS 7481:1996(S2015)	STUDS, STEEL, UNS S66286 AGED AFTER ROLL THREADED PROCUREMENT SPECIFICATION FOR
SAE AMS 5731 : 2012	STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS, TUBING, AND RINGS, 15CR - 25.5NI - 1.2MO - 2.1TI - 0.006B - 0.30V, CONSUMABLE ELECTRODE MELTED, 1800 DEGREES F (982 DEGREES C) SOLUTION HEAT TREATED
SAE AMS 2411 : 2013	PLATING, SILVER FOR HIGH TEMPERATURE APPLICATIONS
SAE AS 7477 : 2016	BOLTS AND SCREWS, STEEL, UNS S66286 TENSILE STRENGTH 130 KSI, PROCUREMENT SPECIFICATION
SAE AMS 2410 : 2010	PLATING, SILVER, NICKEL STRIKE, HIGH BAKE
SAE AS 1310 : 2012	FASTENER TORQUE FOR THREADED APPLICATIONS, DEFINITIONS OF