• There are no items in your cart

VDI 3822 Blatt 2.1.6:2012-01

Current
Current

The latest, up-to-date edition.

Failure analysis - Defects of thermoplastic products made of plastics caused by tribology-induced stress
Available format(s)

Hardcopy , PDF

Language(s)

German - English

Published date

01-01-2012

Preliminary note
Introduction
1 Scope
2 Normative references
3 Terminology
4 Damage resulting from tribological
  stress
5 Examples
Bibliography

In the following, various types of failure that occur in plastic products as a result of tribology induced stress will be described along with the corresponding failure characteristics, the causes of failure and the failure mechanisms.

DevelopmentNote
Applies in conjunction with VDI 3822. (02/2015)
DocumentType
Standard
Pages
23
PublisherName
Verlag des Vereins Deutscher Ingenieure
Status
Current
Supersedes

VDI 3822 Blatt 2.1.8:2012-01 Failure analysis - Defects of thermoplastic products made of plastics caused by weather-induced stress
VDI 3822 Blatt 2.1.1:2012-01 Failure analysis - Defects of thermoplastic products made of plastics caused by faulty design
VDI 3822 Blatt 1.3:2017-06 Failure analysis - Failures on metal products caused by tribology working conditions
VDI 3822 Blatt 2.1.7:2013-01 Failure analysis - Defects of thermoplastic products caused by chemical stress
VDI 3822 Blatt 2.1.4:2012-01 Failure analysis - Defects of thermoplastic products made of plastics caused by mechanical stress
VDI 3822 Blatt 2.1.5:2013-01 Failure analysis - Defects of thermoplastic products caused by thermal stress
VDI 3822 Blatt 2.1.3:2012-01 Failure analysis - Defects of thermoplastic products made of plastics caused by an unfavourable choice of material and by defects in the material
VDI 3822 Blatt 2.1.9:2012-01 Failure analysis - Defects of thermoplastic products made of plastics caused by microbial stress
VDI 3822 Blatt 2.1.10:2012-01 Failure analysis - Significant instrumental analysis methods for failure analysis of products made of plastics

VDI 3822 Blatt 2.1.7:2013-01 Failure analysis - Defects of thermoplastic products caused by chemical stress
VDI 3822 Blatt 1.4:2011-10 Failure analysis - Failures caused by thermal loading
VDI 3822 Blatt 2.1.3:2012-01 Failure analysis - Defects of thermoplastic products made of plastics caused by an unfavourable choice of material and by defects in the material
VDI 3822 Blatt 2.1.8:2012-01 Failure analysis - Defects of thermoplastic products made of plastics caused by weather-induced stress
VDI 3822 Blatt 2.1.4:2012-01 Failure analysis - Defects of thermoplastic products made of plastics caused by mechanical stress
VDI 1000:2017-02 VDI Standardisation Work - Principles and procedures
VDI 3822 Blatt 1.6:2010-11 Failure analysis - Liquid metal induced crack growth by hot dip galvanising
VDI 3822 Blatt 2.1.10:2012-01 Failure analysis - Significant instrumental analysis methods for failure analysis of products made of plastics
VDI 3822 Blatt 2.1.1:2012-01 Failure analysis - Defects of thermoplastic products made of plastics caused by faulty design
VDI 3822 Blatt 2.1.9:2012-01 Failure analysis - Defects of thermoplastic products made of plastics caused by microbial stress
VDI 3822:2011-11 Failure analysis - Fundamentals and performance of failure analysis
VDI 3822 Blatt 2.1.5:2013-01 Failure analysis - Defects of thermoplastic products caused by thermal stress

View more information
US$85.96
Excluding Tax where applicable

Access your standards online with a subscription

Features

  • Simple online access to standards, technical information and regulations.

  • Critical updates of standards and customisable alerts and notifications.

  • Multi-user online standards collection: secure, flexible and cost effective.