ASTM C 1683 : 2010 : R2019

Current
Current

The latest, up-to-date edition.

Standard Practice for Size Scaling of Tensile Strengths Using Weibull Statistics for Advanced Ceramics
Available format(s)

Hardcopy , PDF

Language(s)

English

Published date

07-01-2019

This standard practice provides methodology to convert fracture strength parameters (primarily the mean strength and the Weibull characteristic strength) estimated from data obtained with one test geometry to strength parameters representing other test geometries.

1.1This standard practice provides methodology to convert fracture strength parameters (primarily the mean strength and the Weibull characteristic strength) estimated from data obtained with one test geometry to strength parameters representing other test geometries. This practice addresses uniaxial strength data as well as some biaxial strength data. It may also be used for more complex geometries proved that the effective areas and effective volumes can be estimated. It is for the evaluation of Weibull probability distribution parameters for advanced ceramics that fail in a brittle fashion. Fig. 1 shows the typical variation of strength with size. The larger the specimen or component, the weaker it is likely to be.

1.5The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.

1.5.1The values stated in SI units are in accordance with IEEE/ASTM SI 10.

1.6This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.7This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

Committee
C 28
DocumentType
Standard Practice
Pages
18
PublisherName
American Society for Testing and Materials
Status
Current
Supersedes

ASTM C 1793 : 2015 Standard Guide for Development of Specifications for Fiber Reinforced Silicon Carbide-Silicon Carbide Composite Structures for Nuclear Applications
ASTM C 1783 : 2015 Standard Guide for Development of Specifications for Fiber Reinforced Carbon-Carbon Composite Structures for Nuclear Applications
ASTM C 1323 : 2016 Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature

ASTM C 1499 : 2015 Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1145 : 2019 Standard Terminology of Advanced Ceramics
ASTM C 1211 : 2018 Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures
ASTM C 1211 : 2013 Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures
ASTM C 1322 : 2005 : REV B Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics
ASTM C 1145 : 1998 Standard Terminology of Advanced Ceramics
ASTM C 1161 : 2002 : REV C : R2008 Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1145 : 2006 Standard Terminology of Advanced Ceramics
ASTM E 456 : 2002 Standard Terminology for Relating to Quality and Statistics
ASTM C 1161 : 2002 : REV C : R2008 : EDT 1 Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM E 456 : 2013 : REV A : R2022 Standard Terminology Relating to Quality and Statistics
ASTM C 1499 : 2004 Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1273 : 2018 Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Ambient Temperatures
ASTM C 1161 : 2018 : R2023 Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1322 : 2015 Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics
ASTM C 1322 : 2005 : REV A Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics
ASTM C 1499 : 2003 Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1499 : 2005 Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1145 : 2005 Standard Terminology of Advanced Ceramics
ASTM C 1161 : 2002 : REV C : EDT 1 Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1499 : 2009 Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1273 : 1995 : REV A : R2000 Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Ambient Temperatures
ASTM E 6 : 2002 Standard Terminology Relating to Methods of Mechanical Testing
ASTM C 1323 : 2016 Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature
ASTM C 1366 : 1997 Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Elevated Temperatures
ASTM C 1322 : 2005 : REV B : EDT 1 Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics
ASTM E 456 : 2013 : REV A : R2017 : EDT 5 Standard Terminology Relating to Quality and Statistics
ASTM C 1161 : 2002 : REV A Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1239 : 2006 : REV A Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics
ASTM C 1366 : 2019 Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Elevated Temperatures
ASTM C 1145 : 2003 Standard Terminology of Advanced Ceramics
ASTM C 1323 : 2010 Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature
ASTM C 1273 : 2015 Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Ambient Temperatures
ASTM C 1499 : 2008 Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1239 : 2013 : R2018 Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics
ASTM C 1322 : 2005 : REV B : R2010 Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics
ASTM C 1322 : 1996 : REV A Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics
ASTM C 1161 : 2018 Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1211 : 1998 : REV A Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures
ASTM C 1323 : 1996 Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature
ASTM C 1161 : 2002 Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1322 : 2002 Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics
ASTM C 1499 : 2002 Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM E 6 : 2015 : EDT 3 Standard Terminology Relating to Methods of Mechanical Testing
ASTM C 1366 : 2004 Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Elevated Temperatures
ASTM C 1499 : 2001 Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1239 : 2000 Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics
ASTM E 6 : 2023 : REV A Standard Terminology Relating to Methods of Mechanical Testing
ASTM C 1145 : 2006 : R2013 Standard Terminology of Advanced Ceramics
ASTM C 1161 : 2013 Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1239 : 2000 : R2005 Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics
ASTM C 1323 : 1996 : R2001 Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature
ASTM C 1322 : 2002 : REV A Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics
ASTM C 1499 : 2009 : R2013 Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1145 : 2002 Standard Terminology of Advanced Ceramics
ASTM C 1323 : 1996 : R2001 : EDT 1 Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature
ASTM C 1211 : 2018 : R2023 Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures
ASTM C 1366 : 2004 : R2013 Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Elevated Temperatures
ASTM C 1322 : 2015 : R2019 Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics
ASTM E 6 : 2015 : EDT 4 : REDLINE Standard Terminology Relating to Methods of Mechanical Testing
ASTM C 1211 : 2002 Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures
ASTM C 1273 : 2005 : R2010 Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Ambient Temperatures
ASTM C 1161 : 1994 : R1996 Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1239 : 2006 Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics
ASTM C 1366 : 2004 : R2009 Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Elevated Temperatures
ASTM C 1145 : 2002 : REV A Standard Terminology of Advanced Ceramics
ASTM C 1161 : 2002 : REV C Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1499 : 2019 Standard Test Method for Monotonic Equibiaxial Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1322 : 2005 Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics
ASTM E 6 : 2015 : EDT 4 Standard Terminology Relating to Methods of Mechanical Testing
ASTM E 6 : 2023 Standard Terminology Relating to Methods of Mechanical Testing
ASTM E 456 : 2013 : REV A : R2017 : EDT 4 Standard Terminology Relating to Quality and Statistics
ASTM E 456 : 2013 : REV A : R2017 : EDT 6 Standard Terminology Relating to Quality and Statistics
ASTM C 1145 : 2001 Standard Terminology of Advanced Ceramics
ASTM C 1239 : 2013 Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics
ASTM C 1239 : 2007 Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics
ASTM C 1323 : 2022 Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature
ASTM C 1145 : 2006 : R2013 : EDT 1 Standard Terminology of Advanced Ceramics
ASTM C 1211 : 2002 : R2008 Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures
ASTM C 1273 : 2005 Standard Test Method for Tensile Strength of Monolithic Advanced Ceramics at Ambient Temperatures
ASTM C 1161 : 2002 : REV B Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature

View more information
US$69.00
Excluding Tax where applicable

Access your standards online with a subscription

Features

  • Simple online access to standards, technical information and regulations.

  • Critical updates of standards and customisable alerts and notifications.

  • Multi-user online standards collection: secure, flexible and cost effective.