ASTM D 3171 : 2015 : REDLINE
Current
The latest, up-to-date edition.
English
05-01-2015
CONTAINED IN VOL. 15.03, 2015 Describes the constituent content of composite materials by one of two approaches.
1.1These test methods determine the constituent content of composite materials by one of two approaches. Test Method I physically removes the matrix by digestion or ignition or carbonization by one of eight procedures, leaving the reinforcement essentially unaffected and thus allowing calculation of reinforcement or matrix content (by weight or volume) as well as percent void volume. Test Method II, applicable only to laminate materials of known fiber areal weight, calculates reinforcement or matrix content (by weight or volume), and the cured ply thickness, based on the measured thickness of the laminate. Test Method II is not applicable to the measurement of void volume.
1.1.1These test methods are primarily intended for two-part composite material systems. However, special provisions can be made to extend these test methods to filled material systems with more than two constituents, though not all test results can be determined in every case.
1.1.2The procedures contained within have been designed to be particularly effective for certain classes of polymer or metal matrices. The suggested applications are discussed in Section 4, as well as at the start of each procedure.
1.1.3Test Method I assumes that the reinforcement is essentially unaffected by the digestion or ignition medium or carbonization. A procedure for correction of the results for minor changes in the reinforcement is included. Procedures A through F are based on chemical removal of the matrix while Procedure G removes the matrix by igniting the matrix in a furnace. Procedure H carbonizes the matrix in a furnace.
1.1.4Test Method II assumes that the fiber areal weight of the reinforcement material form is known or controlled to an acceptable tolerance. The presence of voids is not measured. Eq 15 and 16 assume zero void content to perform the calculation.
1.2The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.3This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. See Section 9 for additional information.
| Committee |
D 30
|
| DocumentType |
Redline
|
| Pages |
11
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Current
|
| SupersededBy |
| AASHTO GFRP 1 : 0 | LRFD BRIDGE DESIGN GUIDE SPECIFICATIONS FOR GFRP-REINFORCED CONCRETE BRIDGE DECKS AND TRAFFIC RAILINGS |
| ASTM D 6416/D6416M : 2016 : REDLINE | Standard Test Method for Two-Dimensional Flexural Properties of Simply Supported Sandwich Composite Plates Subjected to a Distributed Load |
| SAE AMS C 3901 : 1998 | ORGANIC FIBER (PARA-ARAMID), YARN AND ROVING, HIGH MODULUS |
| ASTM D 8131/D8131M : 2017 | Standard Practice for Tensile Properties of Tapered and Stepped Joints of Polymer Matrix Composite Laminates |
| ASTM D 3039/D3039M : 2017 : REDLINE | Standard Test Method for Tensile Properties of Polymer Matrix Composite Materials |
| ASTM D 5687/D5687M : 1995 : R2015 | Standard Guide for Preparation of Flat Composite Panels with Processing Guidelines for Specimen Preparation |
| SAE AMS 3867 : 2016 | BORON FILAMENT TAPE, EPOXY-RESIN-IMPREGNATED |
| ACI 440.6M : 2008(R2017) | Specification for Carbon and Glass Fiber-Reinforced Polymer Bar Materials for Concrete Reinforcement<br> |
| ACI 440.6 : 2008 | SPECIFICATION FOR CARBON AND GLASS FIBER-REINFORCED POLYMER BAR MATERIALS FOR CONCRETE REINFORCEMENT |
| ASTM D 7766/D7766M : 2016 : REDLINE | Standard Practice for Damage Resistance Testing of Sandwich Constructions |
| ASTM D 3529 : 2016 | Standard Test Methods for Constituent Content of Composite Prepreg |
| ASTM D 3410/D3410M : 2016 : REDLINE | Standard Test Method for Compressive Properties of Polymer Matrix Composite Materials with Unsupported Gage Section by Shear Loading |
| ASTM D 7248/D7248M : 2012 : R2017 | Standard Test Method for Bearing/Bypass Interaction Response of Polymer Matrix Composite Laminates Using 2-Fastener Specimens |
| ASTM D 6415/D6415M : 2006 : REV A : EDT 1 | Standard Test Method for Measuring the Curved Beam Strength of a Fiber-Reinforced Polymer-Matrix Composite |
| ASTM D 2344/D2344M : 2016 : REDLINE | Standard Test Method for Short-Beam Strength of Polymer Matrix Composite Materials and Their Laminates |
| ASTM D 7137/D7137M : 2017 : REDLINE | Standard Test Method for Compressive Residual Strength Properties of Damaged Polymer Matrix Composite Plates |
| ASTM D 6115 : 1997 | Standard Test Method for Mode I Fatigue Delamination Growth Onset of Unidirectional Fiber-Reinforced Polymer Matrix Composites |
| ASTM D 5379/D5379M : 2012 : REDLINE | Standard Test Method for Shear Properties of Composite Materials by the V-Notched Beam Method |
| ASTM D 7136/D7136M : 2015 : REDLINE | Standard Test Method for Measuring the Damage Resistance of a Fiber-Reinforced Polymer Matrix Composite to a Drop-Weight Impact Event |
| ASTM D 5687/D5687M : 1995 : R2002 | Standard Guide for Preparation of Flat Composite Panels with Processing Guidelines for Specimen Preparation |
| ASTM D 5528 : 2013 : REDLINE | Standard Test Method for Mode I Interlaminar Fracture Toughness of Unidirectional Fiber-Reinforced Polymer Matrix Composites |
| ASTM D 6264/D6264M : 2017 : REDLINE | Standard Test Method for Measuring the Damage Resistance of a Fiber-Reinforced Polymer-Matrix Composite to a Concentrated Quasi-Static Indentation Force |
| ASTM D 7905/D7905M : 2014 | Standard Test Method for Determination of the Mode II Interlaminar Fracture Toughness of Unidirectional Fiber-Reinforced Polymer Matrix Composites |
| ASTM D 8066/D8066M : 2017 | Standard Practice Unnotched Compression Testing of Polymer Matrix Composite Laminates |
| ASTM D 5467/D5467M : 1997 : R2017 | Standard Test Method for Compressive Properties of Unidirectional Polymer Matrix Composite Materials Using a Sandwich Beam |
| ASTM D 6856/D6856M : 2003 : R2008 : EDT 1 | Standard Guide for Testing Fabric-Reinforced "Textile" Composite Materials |
| ASTM D 7078/D7078M : 2012 : REDLINE | Standard Test Method for Shear Properties of Composite Materials by V-Notched Rail Shear Method |
| ASTM D 7914/D7914M : 2014 | Standard Test Method for Strength of Fiber Reinforced Polymer (FRP) Bent Bars in Bend Locations |
| SAE AMS 3903 : 2013 | CLOTH, ORGANIC FIBER (PARA-ARAMID), HIGH MODULUS, EPOXY RESIN IMPREGNATED |
| CSA S808 : 2014 | SPECIFICATION FOR FIBRE-REINFORCED POLYMER (FRP) MATERIALS FOR EXTERNALLY REINFORCING STRUCTURES |
| SAE AMS 3915 : 2015 | ADVANCED COMPOSITES PREPREG - NOMINAL 250 DEGREES F CURE - GLASS FIBER AND EPOXY RESIN, 7781 WEAVE FABRIC |
| ASTM D 7957/D7957M : 2017 | Standard Specification for Solid Round Glass Fiber Reinforced Polymer Bars for Concrete Reinforcement |
| ASTM D 7205/D7205M:2006 | Standard Test Method for Tensile Properties of Fiber Reinforced Polymer Matrix Composite Bars |
| ASTM D 5467/D5467M : 1997 : R2010 | Standard Test Method for Compressive Properties of Unidirectional Polymer Matrix Composites Using a Sandwich Beam |
| ASTM D 5229/D5229M : 2014-06 | TEST METHOD FOR MOISTURE ABSORPTION PROPERTIES AND EQUILIBRIUM CONDITIONING OF POLYMER MATRIX COMPOSITE MATERIALS |
| ASTM D 6264 : 1998 | Standard Test Method for Measuring the Damage Resistance of a Fiber-Reinforced Polymer-Matrix Composite to a Concentrated Quasi-Static Indentation Force |
| ASTM D 7205/D7205M : 2006 : R2016 | Standard Test Method for Tensile Properties of Fiber Reinforced Polymer Matrix Composite Bars |
| SAE AMS 3894 : 2016 | Carbon Fiber Tape and Sheet Epoxy Resin Impregnated |
| ASTM C 364/C364M : 2016 : REDLINE | Standard Test Method for Edgewise Compressive Strength of Sandwich Constructions |
| ASTM D 6856 : 2003 : R2008 | Standard Guide for Testing Fabric-Reinforced "Textile" Composite Materials |
| ASTM D 7205/D7205M : 2006 : R2011 | Standard Test Method for Tensile Properties of Fiber Reinforced Polymer Matrix Composite Bars |
| ASTM D 6115 : 1997 : R2004 | Standard Test Method for Mode I Fatigue Delamination Growth Onset of Unidirectional Fiber-Reinforced Polymer Matrix Composites |
| ASTM D 3529/D3529M : 1997 : R2003 : EDT 1 | Standard Test Method for Matrix Solids Content and Matrix Content of Composite Prepreg |
| ASTM D 5450/D5450M : 2016 : REDLINE | Standard Test Method for Transverse Tensile Properties of Hoop Wound Polymer Matrix Composite Cylinders |
| ASTM F 988 : 1986 | Guide for Specifying Carbon-Fiber Randomly Reinforced Ultra-High-Molecular-Weight Polyethylene for Medical Devices (Withdrawn 1992) |
| ASTM D 3529/D3529M : 1997 : R2008 | Standard Test Method for Matrix Solids Content and Matrix Content of Composite Prepreg |
| ASTM D 6856/D6856M : 2003 : R2016 | Standard Guide for Testing Fabric-Reinforced “Textile” Composite Materials |
| ASTM D 345 : 2002 | Side bearings of the freight wagon bogies. General specifications |
| ASTM D 6484/D6484M : 2014 : REDLINE | Standard Test Method for Open-Hole Compressive Strength of Polymer Matrix Composite Laminates |
| ASTM D 5449/D5449M : 2016 : REDLINE | Standard Test Method for Transverse Compressive Properties of Hoop Wound Polymer Matrix Composite Cylinders |
| ASTM D 3529/D3529M : 1997 | Standard Test Method for Matrix Solids Content and Matrix Content of Composite Prepreg |
| SAE AMS 3897 : 2016 | CLOTH, CARBON FIBER, RESIN IMPREGNATED |
| ACI 440.2R : 2017 | GUIDE FOR THE DESIGN AND CONSTRUCTION OF EXTERNALLY BONDED FRP SYSTEMS FOR STRENGTHENING CONCRETE STRUCTURES |
| SAE AMS 3960 : 2015 | Advanced Composites Prepreg - Nominal 250 °F Cure - Carbon Fiber and Epoxy Resin, Unidirectional Tape |
| ASTM C 1783 : 2015 | Standard Guide for Development of Specifications for Fiber Reinforced Carbon-Carbon Composite Structures for Nuclear Applications |
| ASTM C 1793 : 2015 | Standard Guide for Development of Specifications for Fiber Reinforced Silicon Carbide-Silicon Carbide Composite Structures for Nuclear Applications |
| ASTM D 7332/D7332M : 2016 : REDLINE | Standard Test Method for Measuring the Fastener Pull-Through Resistance of a <brk/>Fiber-Reinforced Polymer Matrix Composite |
| ASTM D 7291/D7291M : 2015 : REDLINE | Standard Test Method for Through-Thickness “Flatwise” Tensile Strength and Elastic Modulus of a Fiber-Reinforced Polymer Matrix Composite Material |
| ASTM D 6115 : 1997 : R2011 | Standard Test Method for Mode I Fatigue Delamination Growth Onset of Unidirectional Fiber-Reinforced Polymer Matrix Composites |
| CSA S806: 2012 | DESIGN AND CONSTRUCTION OF BUILDING STRUCTURES WITH FIBRE-REINFORCED POLYMERS |
| S806-12 (R2017) | Design and construction of building structures with fibre-reinforced polymers |
| ASTM D 5467/D5467M : 1997 : R2004 | Standard Test Method for Compressive Properties of Unidirectional Polymer Matrix Composites Using a Sandwich Beam |
| ADS-13F-HDBK : 1997 | AERONAUTICAL DESIGN STANDARD - HANDBOOK - AIR VEHICLE MATERIALS AND PROCESSES |
| ACI 440.6M : 2008 : MET | SPECIFICATION FOR CARBON AND GLASS FIBER-REINFORCED POLYMER BAR MATERIALS FOR CONCRETE REINFORCEMENT |
| SAE AMS 2980/1 : 2014 | CARBON FIBER FABRIC AND EPOXY RESIN WET LAY-UP REPAIR MATERIAL - PART 1 - GENERAL REQUIREMENTS |
| ASTM D 7248/D7248M : 2012 | Standard Test Method for Bearing/Bypass Interaction Response of Polymer Matrix Composite Laminates Using 2-Fastener Specimens |
| ASTM D 5687/D5687M :1995 | Standard Guide for Preparation of Flat Composite Panels with Processing Guidelines for Specimen Preparation |
| ASTM D 6742/D6742M : 2017 : REDLINE | Standard Practice for Filled-Hole Tension and Compression Testing of Polymer Matrix Composite Laminates |
| ASTM D 5687/D5687M : 1995 : R2007 | Standard Guide for Preparation of Flat Composite Panels with Processing Guidelines for Specimen Preparation |
| SAE AMS 3970/1 : 2011 | CARBON FIBER FABRIC REPAIR PREPREG, 120 DEGREES C (250 DEGREES F) VACUUM CURING - PART 1 - GENERAL REQUIREMENTS |
| MIL-P-46184 Base Document:1982 | PLASTIC MOLDING & EXTRUSION MATERIAL, POLYETHERIMIDE (PEI) |
| SAE AMS 3914A : 2015 | ADVANCED COMPOSITES PREPREG - NOMINAL 250 DEGREES F CURE - 12K TOW CARBON FIBER AND EPOXY RESIN, PLAIN WEAVE FABRIC |
| ASTM D 5961/D5961M : 2017 : REDLINE | Standard Test Method for Bearing Response of Polymer Matrix Composite Laminates |
| ASTM D 5448/D5448M : 2016 : REDLINE | Standard Test Method for Inplane Shear Properties of Hoop Wound Polymer Matrix Composite Cylinders |
| ASTM D 6856 : 2003 | Standard Guide for Testing Fabric-Reinforced "Textile" Composite Materials |
| ASTM C 613M : 1997 : R2008 : EDT 1 | Standard Test Method for Constituent Content of Composite Prepreg by Soxhlet Extraction |
| ASTM D 8101/D8101M : 2017 | Standard Test Method for Measuring the Penetration Resistance of Composite Materials to Impact by a Blunt Projectile |
| ASTM D 8033 : 2016 | Standard Classification System for Poly(Ether Ether Ketone) (PEEK) Molding and Extrusion Materials |
| ASTM C 297/C297M : 2016 : REDLINE | Standard Test Method for Flatwise Tensile Strength of Sandwich Constructions |
| ASTM D 6415/D6415M : 2006 | Standard Test Method for Measuring the Curved Beam Strength of a Fiber-Reinforced Polymer-Matrix Composite |
| ASTM D 6415/D6415M : 2006 : REV A : R2013 | Standard Test Method for Measuring the Curved Beam Strength of a Fiber-Reinforced Polymer-Matrix Composite |
| ASTM E 177 : 2014 : REDLINE | Standard Practice for Use of the Terms Precision and Bias in ASTM Test Methods |
| ASTM D 5229/D5229M : 2014-06 | TEST METHOD FOR MOISTURE ABSORPTION PROPERTIES AND EQUILIBRIUM CONDITIONING OF POLYMER MATRIX COMPOSITE MATERIALS |
| ASTM D 792 : 2013 : REDLINE | Standard Test Methods for Density and Specific Gravity (Relative Density) of Plastics by Displacement |
| ASTM E 12 : 1970 : R1991 : EDT 1 | Terminology Relating to Density and Specific Gravity of Solids, Liquids, and Gases (Withdrawn 1996) |
Please Login or Create an Account so you can add users to your Multi user PDF Later.
Important note : All end users must be registered with an Account prior to user licenses being assigned.
Users cannot be edited or removed once added to your Multi user PDF.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.