ASTM E 2818 : 2011
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
Hardcopy , PDF
11-13-2019
English
05-01-2011
CONTAINED IN VOL. 03.01, 2015 Defines methods for preparing specimens from welds in metallic materials and interpreting subsequent test results when used in conjunction with standards Test Methods E 1290 and E 1820 for the determination of fracture toughness.
1.1 This practice provides methods for preparing specimens from welds in metallic materials and interpreting subsequent test results when used in conjunction with standards Test Methods E1290 and E1820 for the determination of fracture toughness. The fatigue pre-cracking procedures included in this practice may also be used to aid in preparing straight pre-cracks for weld specimens in accordance with Test Method E1681.
1.2 This practice draws heavily from ISO 15653: Metallic materials – Method of test for the determination of quasistatic fracture toughness of welds. All references to ISO 12135 in that test method should be replaced with the applicable ASTM Test Methods (E1820, E1290 or E1681).
1.3 The recommended specimen is a single-edge bend [SE(B)] with width, W, equal to twice the specimen thickness, B. An alternate SE(B) specimen with W/B equal to one and a span, S, to W ratio of 4 may be used but may produce different toughness values. A compact tension [C(T)] specimen may be used if it can be demonstrated that the analysis of results properly accounts for weld-to-base metal strength mismatch effects on fracture toughness.
| Committee |
E 08
|
| DocumentType |
Standard Practice
|
| Pages |
4
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Superseded
|
| SupersededBy |
| ASTM E 1457 : 2015 | Standard Test Method for Measurement of Creep Crack Growth Times in Metals |
| ASTM E 1457 : 2015 : REDLINE | Standard Test Method for Measurement of Creep Crack Growth Times in Metals |
| ASTM E 1820 : 2013 | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1820 : 2009 : EDT 1 | Standard Test Method for Measurement of Fracture Toughness |
| ISO 15653:2010 | Metallic materials Method of test for the determination of quasistatic fracture toughness of welds |
| ASTM E 1681: 2003 | Standard Test Method for Determining a Threshold Stress Intensity Factor for Environment-Assisted Cracking of Metallic Materials |
| ASTM E 1681 : 2003 : R2008 : EDT 1 | Standard Test Method for Determining a Threshold Stress Intensity Factor for Environment-Assisted Cracking of Metallic Materials |
| ASTM E 1823 : 2012 : REV : EDT 0 | Standard Terminology Relating to Fatigue and Fracture Testing |
| ASTM E 1823 : 2007 : REV A | Standard Terminology Relating to Fatigue and Fracture Testing |
| ASTM E 1681 : 2003 : R2008 | Standard Test Method for Determining a Threshold Stress Intensity Factor for Environment-Assisted Cracking of Metallic Materials |
| ASTM E 1290 : 2002 : EDT 1 | Standard Test Method for Crack-Tip Opening Displacement (CTOD) Fracture Toughness Measurement |
| ASTM E 1820 : 2011 : EDT 2 | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1823 : 2009 : REV A | Standard Terminology Relating to Fatigue and Fracture Testing |
| ASTM E 1681 : 2003 : R2013 | Standard Test Method for Determining Threshold Stress Intensity Factor for Environment-Assisted Cracking of Metallic Materials |
| ASTM E 1820 : 2011 : EDT 1 | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1820 : 2006 | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1820 : 2018 | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1820 : 2011 | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1820 : 2008 : REV A | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1681 : 2003 : R2008 : EDT 2 | Standard Test Method for Determining Threshold Stress Intensity Factor for Environment-Assisted Cracking of Metallic Materials |
| ASTM E 1820 : 2017 | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1823 : 2005 : REV A : EDT 1 | Standard Terminology Relating to Fatigue and Fracture Testing |
| ASTM E 1823 : 2010 : REV A | Standard Terminology Relating to Fatigue and Fracture Testing |
| ASTM E 1823 : 2009 : REV B | Standard Terminology Relating to Fatigue and Fracture Testing |
| ASTM E 1820 : 2017 : REV A | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1820 : 2005 | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1823 : 2012 : REV D | Standard Terminology Relating to Fatigue and Fracture Testing |
| ASTM E 1823 : 2012 : REV B | Standard Terminology Relating to Fatigue and Fracture Testing |
| ASTM E 1290 : 2008 : EDT 1 | Standard Test Method for Crack-Tip Opening Displacement (CTOD) Fracture Toughness Measurement (Withdrawn 2013) |
| ASTM E 1820 : 2015 | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1290 : 2002 | Standard Test Method for Crack-Tip Opening Displacement (CTOD) Fracture Toughness Measurement |
| ASTM E 1820 : 2006 : EDT 1 | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1290 : 1999 | Standard Test Method for Crack-Tip Opening Displacement (CTOD) Fracture Toughness Measurement |
| ASTM E 1290 : 2008 | Standard Test Method for Crack-Tip Opening Displacement (CTOD) Fracture Toughness Measurement |
| ASTM E 1823 : 1996 : R2002 | Standard Terminology Relating to Fatigue and Fracture Testing |
| ASTM E 1823 : 1996 : EDT 1 | Standard Terminology Relating to Fatigue and Fracture Testing |
| ASTM E 1823 : 2012 : REV A | Standard Terminology Relating to Fatigue and Fracture Testing |
| ISO 12135:2016 | Metallic materials Unified method of test for the determination of quasistatic fracture toughness |
| ASTM E 1823 : 2007 | Standard Terminology Relating to Fatigue and Fracture Testing |
| ASTM E 1820 : 2015 : REV A : EDT 1 | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1820 : 2018 : REV A | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1820 : 2016 | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1681 : 1999 : EDT 1 | Standard Test Method for Determining a Threshold Stress Intensity Factor for Environment-Assisted Cracking of Metallic Materials |
| ASTM E 1820 : 1999 : REV A | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1820 : 2001 | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1820 : 2013 : EDT 1 | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1820 : 2015 : REV A | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1823 : 2013 | Standard Terminology Relating to Fatigue and Fracture Testing |
| ASTM E 1820 : 2009 | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1820 : 2005 : REV A | Standard Test Method for Measurement of Fracture Toughness |
| ASTM E 1823 : 2012 : REV C | Standard Terminology Relating to Fatigue and Fracture Testing |
| ASTM E 1290 : 2007 | Standard Test Method for Crack-Tip Opening Displacement (CTOD) Fracture Toughness Measurement |
| ASTM E 8/E8M : 2016-09 | TEST METHODS FOR TENSION TESTING OF METALLIC MATERIALS |
| ASTM E 1823 : 2005 : REV A | Standard Terminology Relating to Fatigue and Fracture Testing |
| ASTM E 1823 : 2011 | Standard Terminology Relating to Fatigue and Fracture Testing |
Please Login or Create an Account so you can add users to your Multi user PDF Later.
Important note : All end users must be registered with an Account prior to user licenses being assigned.
Users cannot be edited or removed once added to your Multi user PDF.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.