Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature

Available format(s)

Hardcopy , PDF

Language(s)

English

Published date

03-21-2022

Publisher

American Society for Testing and Materials

1.1This test method covers the determination of ultimate strength under monotonic loading of advanced ceramics in tubular form at ambient temperatures. The ultimate strength as used in this test method refers to the strength obtained under monotonic compressive loading of C-ring specimens such as shown in Fig. 1, where monotonic refers to a continuous nonstop test rate with no reversals from test initiation to final fracture. This method permits a range of sizes and shapes since test specimens may be prepared from a variety of tubular structures. The method may be used with microminiature test specimens.

FIG. 1C-Ring Test Geometry with Defining Geometry and Reference Angle (θ) for the Point of Fracture Initiation on the Circumference

C-Ring Test Geometry with Defining Geometry and Reference Angle () for the Point of Fracture Initiation on the Circumference

1.2The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.

1.2.1Values expressed in this test method are in accordance with the International System of Units (SI) and IEEE/ASTM SI 10.

1.3This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.4This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

Committee	C 28
DocumentType	Test Method
Pages	8
PublisherName	American Society for Testing and Materials
Status	Current
Supersedes	ASTM C 1323 : 2016

ASTM C 1683 : 2010 : R2019

Standard Practice for Size Scaling of Tensile Strengths Using Weibull Statistics for Advanced Ceramics

ASTM C 1161 : 2018 : R2023	Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM E 337 : 2015 : R2023	Standard Test Method for Measuring Humidity with a Psychrometer (the Measurement of Wet- and Dry-Bulb Temperatures)
ASTM E 337 : 2015	Standard Test Method for Measuring Humidity with a Psychrometer (the Measurement of Wet- and Dry-Bulb Temperatures)
ASTM C 1161 : 2018	Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM E 6 : 2023 : REV A	Standard Terminology Relating to Methods of Mechanical Testing
ASTM E 6 : 2015 : EDT 4 : REDLINE	Standard Terminology Relating to Methods of Mechanical Testing
ASTM E 6 : 2015 : EDT 4	Standard Terminology Relating to Methods of Mechanical Testing
ASTM E 6 : 2023	Standard Terminology Relating to Methods of Mechanical Testing