ASTM C 1368 : 2010

Superseded
Superseded

A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.

Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Strength Testing at Ambient Temperature
Available format(s)

Hardcopy , PDF

Superseded date

11-11-2014

Language(s)

English

Published date

12-01-2010

1.1 This test method covers the determination of slow crack growth (SCG) parameters of advanced ceramics by using constant stress-rate rectangular beam flexural testing, or ring-on-ring biaxial disk flexural testing, or direct tensile strength, in which strength is determined as a function of applied stress rate in a given environment at ambient temperature. The strength degradation exhibited with decreasing applied stress rate in a specified environment is the basis of this test method which enables the evaluation of slow crack growth parameters of a material.

Note 1—This test method is frequently referred to as dynamic fatigue testing (Refs (1-3) ) in which the term fatigue is used interchangeably with the term slow crack growth. To avoid possible confusion with the fatigue phenomenon of a material which occurs exclusively under cyclic loading, as defined in Terminology E1823, this test method uses the term constant stress-rate testing rather than dynamic fatigue testing.

Note 2—In glass and ceramics technology, static tests of considerable duration are called static fatigue tests, a type of test designated as stress-rupture (See Terminology E1823).

1.2 Values expressed in this test method are in accordance with the International System of Units (SI) and .

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Committee
C 28
DocumentType
Test Method
Pages
11
ProductNote
Reconfirmed 2010
PublisherName
American Society for Testing and Materials
Status
Superseded
Supersedes

ASTM C 1674 : 2016 Standard Test Method for Flexural Strength of Advanced Ceramics with Engineered Porosity (Honeycomb Cellular Channels) at Ambient Temperatures
ASTM C 1576 : 2005 : R2017 Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress Flexural Testing (Stress Rupture) at Ambient Temperature
ASTM C 1161 : 2018 Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature
ASTM C 1834 : 2016 Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress Flexural Testing (Stress Rupture) at Elevated Temperatures
ASTM C 1323 : 2016 Standard Test Method for Ultimate Strength of Advanced Ceramics with Diametrally Compressed C-Ring Specimens at Ambient Temperature
ASTM C 1684 : 2018 Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature—Cylindrical Rod Strength
ASTM C 1014 : 2017 Standard Specification for Spray-Applied Mineral Fiber Thermal and Sound Absorbing Insulation
ASTM C 1465 : 2008 : R2019 Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Flexural Testing at Elevated Temperatures
ASTM C 1211 : 2018 Standard Test Method for Flexural Strength of Advanced Ceramics at Elevated Temperatures

View more information
US$83.00
Excluding Tax where applicable

Access your standards online with a subscription

Features

  • Simple online access to standards, technical information and regulations.

  • Critical updates of standards and customisable alerts and notifications.

  • Multi-user online standards collection: secure, flexible and cost effective.