AS/NZS 1580.602.2:1995

1 - AS/NZS 1580.602.2:1995 PAINTS AND RELATED MATERIALS-METHODS OF TEST - MEASUREMENT OF SPECULAR GLOSS OF NON-METALLIC PAINT FILMS
1 - PREFACE
3 - METHOD
3 - 1 Scope
3 - 2 Normative references
3 - 3 Definition
3 - 3.1 specular gloss:
3 - 4 Required supplementary information
4 - 5 Apparatus
4 - 5.1 Substrate for tests where a liquid paint sample is supplied
4 - 5.2 Film applicator
4 - 5.3 Glossmeter
6 - 5.4 Reference standards
6 - 5.4.1 Primary reference standard
6 - 5.4.2 Working reference standards
6 - 5.4.3 Zero reference standard
7 - 6 Sampling of liquid paints
7 - 7 Sampling of coated substrates
7 - 8 Preparation of test panels
7 - 8.1 Liquid paint samples
7 - 8.1.1 Preparation of test films
7 - 8.1.2 Thickness measurement
7 - 8.2 Paint films on substrates
7 - 8.2.1 General
7 - 8.2.2 Thickness measurement
7 - 9 Calibration of the gloss meter
7 - 9.1 Preparation of the apparatus
7 - 9.2 Zero-point check
7 - 9.3 Calibration
8 - 10 Procedure
8 - 10.1 Gloss measurement of films from liquid paints
8 - 10.2 Gloss measurement on coated substrates
8 - 11 Precision
8 - 11.1 Repeatability
8 - 11.2 Reproducibility
8 - 12 Test report
9 - Annex A - Required supplementary information
10 - Annex B - Bibliography

Provides procedures for determining the specular gloss of non-metallic paint films using a glossmeter. Identical with and reproduced from ISO2813:1994.

This International Standard is one of a series of standards dealing with the sampling and testing of paints, varnishes and related products.It specifies a test method for determining the specular gloss of paint films using a reflectometer geometry of 20¦, 60¦ or 85¦. The method is not suitable for the measurement of the gloss of metallic paints.a) The 60¦ geometry is applicable to all paint films, but for very high gloss and near-matt films 20¦ or85 ¦ may be more suitable.b) The 20¦ geometry, which uses a smaller receptor aperture, is intended to give improved differentiation between high-gloss paint films (i.e. films with a 60¦ specular gloss higher than about 70 units).c) The 85¦ geometry is intended to give improved differentiation between low-gloss paint films (i.e. films with a 60¦ specular gloss lower than about 10 units).NOTES1 The same geometry should, of course, be retained for a series of measurements even if this means disregarding the suggested limits.2 In some cases, the determination of specular gloss may not correspond to a visual assessment.

First published as AS K41.602.2-1972.Revised and redesignated AS 1580.602.2-1974.Revised and designated as Joint Standard AS/NZS 1580.602.2:1995.Reconfirmed 2013. Originated in Australia as AS K41.602.2-1972. Previous edit ion AS 1580.602.2-1974. Jointly revised and designated AS/NZS 1580.602.2:1995.