EN ISO 642:1999
Current
Current
The latest, up-to-date edition.
Steel - Hardenability test by end quenching (Jominy test) (ISO 642:1999)
Published date
01-09-1999
Publisher
Foreword
1 Scope
2 Normative references
3 Principle
4 Symbols and designations
5 Form of test pieces and their preparation
6 Apparatus
7 Heating and quenching of test pieces
8 Preparation for, and measurement of, hardness after quenching
9 Expression of results
10 Test report
Annex A (informative) - Specification for the hardenability
of a product
Annex B (informative) - Additional information to clause 10
Annex C (informative) - Calculation of the hardenability
Annex ZA (normative) - Normative references to international
publications with their relevant European publications
Bibliography
Method for determining the hardenability of steel by the end quench, (Jominy test), by using a test piece of 25 mm diameter and 100 mm long.
| Committee |
CEN/TC 459/SC 1
|
| DocumentType |
Standard
|
| PublisherName |
Comite Europeen de Normalisation
|
| Status |
Current
|
| Standards | Relationship |
| UNE-EN ISO 642:2000 | Identical |
| DIN EN ISO 642:2000-01 | Identical |
| NF EN ISO 642 : 1999 | Identical |
| ISO 642:1999 | Identical |
| NBN EN ISO 642 : 1ED 99 | Identical |
| NEN EN ISO 642 : 1999 | Identical |
| NS EN ISO 642 : 1ED 2000 | Identical |
| I.S. EN ISO 642:2000 | Identical |
| PN EN ISO 642 : 2002 | Identical |
| SN EN ISO 642 : 1999 | Identical |
| UNI EN ISO 642 : 2003 | Identical |
| BS EN ISO 642:1999 | Identical |
| DIN EN ISO 642 E : 2000 | Identical |
| BS EN 2213:2012 | Aerospace series. Steel FE-PL1505 (15CrMoV6). Air melted. Hardened and tempered. Bars. De ≤ 16 mm. 980 MPa ≤ Rm ≤ 1 180 MPa |
| BS EN 4500-005:2012 | Aerospace series. Metallic materials. Rules for drafting and presentation of material standards Specific rules for steels |
| 13/30290101 DC : 0 | BS EN 4700-2 - AEROSPACE SERIES - STEEL AND HEAT RESISTING ALLOYS - WROUGHT PRODUCTS - TECHNICAL SPECIFICATION - PART 002: BAR AND SECTION |
| I.S. EN 2213:2012 | AEROSPACE SERIES - STEEL FE-PL1505 (15CRMOV6) - AIR MELTED - HARDENED AND TEMPERED - BARS - D[E] <= 16 MM - 980 MPA <= R[M] <= 1180 MPA |
| I.S. EN 4700-007:2010 | AEROSPACE SERIES - STEEL AND HEAT RESISTING ALLOYS - WROUGHT PRODUCTS - TECHNICAL SPECIFICATION - PART 007: REMELTING STOCK |
| NF EN 2205 : 2009 | AEROSPACE SERIES - STEEL FE-PL1502 (25CRMO4) - 900 MPA <= R[M] <= 1100 MPA - BARS - D[E] <= 40 MM |
| NF EN 4700-007 : 2012 | AEROSPACE SERIES - STEEL AND HEAT RESISTING ALLOYS - WROUGHT PRODUCTS - TECHNICAL SPECIFICATION - PART 007: REMELTING STOCK |
| BS EN 10089:2002 | Hot rolled steels for quenched and tempered springs. Technical delivery conditions |
| I.S. EN 10084:2008 | CASE HARDENING STEELS - TECHNICAL DELIVERY CONDITIONS |
| EN 10297-1:2003 | Seamless circular steel tubes for mechanical and general engineering purposes - Technical delivery conditions - Part 1: Non-alloy and alloy steel tubes |
| EN 10263-1:2017 | Steel rod, bars and wire for cold heading and cold extrusion - Part 1: General technical delivery conditions |
| EN 10083-2:2006 | Steels for quenching and tempering - Part 2: Technical delivery conditions for non alloy steels |
| UNI EN 2213 : 2013 | AEROSPACE SERIES - STEEL FE-PL1505 (15CRMOV6) - AIR MELTED - HARDENED AND TEMPERED - BARS - D[E] <= 16 MM - 980 MPA <= R[M] <= 1180 MPA |
| EN 4700-002:2016 | Aerospace series - Steel and heat resisting alloys - Wrought products - Technical specification - Part 002: Bar and section |
| 05/30132585 DC : DRAFT APR 2005 | EN 10083-1 - STEELS FOR QUENCHING AND TEMPERING - PART 1: GENERAL TECHNICAL DELIVERY CONDITIONS |
| PREN 764-4 : DRAFT 2012 | PRESSURE EQUIPMENT - PART 4: ESTABLISHMENT OF TECHNICAL DELIVERY CONDITIONS FOR METALLIC MATERIALS |
| UNI EN 4700-007 : 2011 | AEROSPACE SERIES - STEEL AND HEAT RESISTING ALLOYS - WROUGHT PRODUCTS - TECHNICAL SPECIFICATION - PART 007: REMELTING STOCK |
| NF EN 4700-002 : 2012 | AEROSPACE SERIES - STEEL AND HEAT RESISTING ALLOYS - WROUGHT PRODUCTS - TECHNICAL SPECIFICATION - PART 002: BAR AND SECTION |
| EN 10083-1:2006 | Steels for quenching and tempering - Part 1: General technical delivery conditions |
| DIN EN 10297-1 E : 2003 | SEAMLESS CIRCULAR STEEL TUBES FOR MECHANICAL AND GENERAL ENGINEERING PURPOSES - TECHNICAL DELIVERY CONDITIONS - PART 1: NON-ALLOY AND ALLOY STEEL TUBES |
| DIN EN 10297-1:2003-06 | SEAMLESS CIRCULAR STEEL TUBES FOR MECHANICAL AND GENERAL ENGINEERING PURPOSES - TECHNICAL DELIVERY CONDITIONS - PART 1: NON-ALLOY AND ALLOY STEEL TUBES |
| I.S. EN 10083-2:2006 | STEELS FOR QUENCHING AND TEMPERING - PART 2: TECHNICAL DELIVERY CONDITIONS FOR NON ALLOY STEELS |
| DIN EN 10083-3:2007-01 | STEELS FOR QUENCHING AND TEMPERING - PART 3: TECHNICAL DELIVERY CONDITIONS FOR ALLOY STEELS |
| I.S. EN 764-4:2014 | PRESSURE EQUIPMENT - PART 4: ESTABLISHMENT OF TECHNICAL DELIVERY CONDITIONS FOR METALLIC MATERIALS |
| 12/30259070 DC : 0 | BS EN 764-4 - PRESSURE EQUIPMENT - PART 4: ESTABLISHMENT OF TECHNICAL DELIVERY CONDITIONS FOR METALLIC MATERIALS |
| BS EN 4700-002:2016 | Aerospace series. Steel and heat resisting alloys. Wrought products. Technical specification Bar and section |
| I.S. EN 10083-1:2006 | STEELS FOR QUENCHING AND TEMPERING - PART 1: GENERAL TECHNICAL DELIVERY CONDITIONS |
| EN 13001-3-5:2016 | Cranes - General design - Part 3-5: Limit states and proof of competence of forged hooks |
| 05/30132603 DC : DRAFT APR 2005 | EN 10083-3 - STEELS FOR QUENCHING AND TEMPERING - PART 3: TECHNICAL DELIVERY CONDITIONS FOR ALLOY STEELS |
| BS EN 10083-3 : 2006-08 | STEELS FOR QUENCHING AND TEMPERING - PART 3: TECHNICAL DELIVERY CONDITIONS FOR ALLOY STEELS |
| I.S. EN 2205:2009 | AEROSPACE SERIES - STEEL FE-PL1502 (25CRMO4) - 900 MPA <= R[M] <= 1100 MPA - BARS - D[E] <= 40 MM |
| DIN EN 10083-1:2006-10 | STEELS FOR QUENCHING AND TEMPERING - PART 1: GENERAL TECHNICAL DELIVERY CONDITIONS |
| DIN EN 10089:2003-04 | Hot rolled steels for quenched and tempered springs - Technical delivery conditions; German version EN 10089:2002 |
| UNE-EN 764-4:2015 | Pressure equipment - Part 4: Establishment of technical delivery conditions for metallic materials |
| UNI EN 10083-1 : 2006 | STEELS FOR QUENCHING AND TEMPERING - PART 1: GENERAL TECHNICAL DELIVERY CONDITIONS |
| UNI EN 10083-3 : 2006 | STEELS FOR QUENCHING AND TEMPERING - PART 3: TECHNICAL DELIVERY CONDITIONS FOR ALLOY STEELS |
| UNI EN 10084 : 2008 | CASE HARDENING STEELS - TECHNICAL DELIVERY CONDITIONS |
| I.S. EN 4700-002:2016 | AEROSPACE SERIES - STEEL AND HEAT RESISTING ALLOYS - WROUGHT PRODUCTS - TECHNICAL SPECIFICATION - PART 002: BAR AND SECTION |
| 14/30294825 DC : 0 | BS EN 10263-1 - STEEL ROD, BARS AND WIRE FOR COLD HEADING AND COLD EXTRUSION - PART 1: GENERAL TECHNICAL DELIVERY CONDITIONS |
| BS EN 2205:2009 | Aerospace series. Steel FE-PL1502 (25CrMo4). 900 MPa ≤ Rm ≤ 1100 MPa. Bars. De ≤ 40 mm |
| UNI EN 4500-005 : 2014 | AEROSPACE SERIES - METALLIC MATERIALS - RULES FOR DRAFTING AND PRESENTATION OF MATERIAL STANDARDS - PART 005: SPECIFIC RULES FOR STEELS |
| EN 10083-3:2006/AC:2008 | STEELS FOR QUENCHING AND TEMPERING - PART 3: TECHNICAL DELIVERY CONDITIONS FOR ALLOY STEELS |
| I.S. EN 10263-1:2017 | STEEL ROD, BARS AND WIRE FOR COLD HEADING AND COLD EXTRUSION - PART 1: GENERAL TECHNICAL DELIVERY CONDITIONS |
| DIN EN 10084:2008-06 | CASE HARDENING STEELS - TECHNICAL DELIVERY CONDITIONS |
| BS EN 10084 : 2008-06 | CASE HARDENING STEELS - TECHNICAL DELIVERY CONDITIONS |
| BS EN 10083-2:2006 | Steels for quenching and tempering Technical delivery conditions for non alloy steels |
| BS EN 764-4:2014 | Pressure equipment Establishment of technical delivery conditions for metallic materials |
| BS EN 10083-1:2006 | Steels for quenching and tempering General technical delivery conditions |
| EN 4500-005:2012 | Aerospace series - Metallic materials - Rules for drafting and presentation of material standards - Part 005: Specific rules for steels |
| EN 4700-007:2010 | Aerospace series - Steel and heat resisting alloys - Wrought products - Technical specification - Part 007: Remelting stock |
| EN 2213 : 2012 | AEROSPACE SERIES - STEEL FE-PL1505 (15CRMOV6) - AIR MELTED - HARDENED AND TEMPERED - BARS - D[E] <= 16 MM - 980 MPA <= R[M] <= 1180 MPA |
| EN 2205 : 2009 | Aerospace series - Steel FE-PL1502 (25CrMo4) - 900 MPa ≤ Rm ≤ 1 100 MPa - Bars - De ≤ 40 mm |
| EN 764-4:2014 | Pressure equipment - Part 4: Establishment of technical delivery conditions for metallic materials |
| PREN 10263-1 : DRAFT 2014 | STEEL ROD, BARS AND WIRE FOR COLD HEADING AND COLD EXTRUSION - PART 1: GENERAL TECHNICAL DELIVERY CONDITIONS |
| I.S. EN 4500-005:2012 | AEROSPACE SERIES - METALLIC MATERIALS - RULES FOR DRAFTING AND PRESENTATION OF MATERIAL STANDARDS - PART 005: SPECIFIC RULES FOR STEELS |
| BS EN 4700-007:2010 | Aerospace series. Steel and heat resisting alloys. Wrought products. Technical specification Remelting stock |
| BS EN 13001-3-5:2016 | Cranes. General design Limit states and proof of competence of forged hooks |
| 05/30132598 DC : DRAFT APR 2005 | EN 10083-2 - STEELS FOR QUENCHING AND TEMPERING - PART 2: TECHNICAL DELIVERY CONDITIONS FOR NON ALLOYS STEELS |
| PREN 2213 : 200P1 | AEROSPACE SERIES - STEEL FE-PL1505 (15CRMOV6) - AIR MELTED - HARDENED AND TEMPERED - BARS - D[E] <= 16 MM - 980 MPA <= R[M] <= 1180 MPA |
| PREN 4500-005 : 200P2 | AEROSPACE SERIES - METALLIC MATERIALS - RULES FOR DRAFTING AND PRESENTATION OF MATERIAL STANDARDS - PART 005: SPECIFIC RULES FOR STEELS |
| PREN 4700-002 : 200P3 | AEROSPACE SERIES - STEEL AND HEAT RESISTING ALLOYS WROUGHT PRODUCTS - TECHNICAL SPECIFICATION - PART 002: BAR AND SECTION |
| BS EN 10263-1:2017 | Steel rod, bars and wire for cold heading and cold extrusion General technical delivery conditions |
| I.S. EN 10083-3:2006 | STEELS FOR QUENCHING AND TEMPERING - PART 3: TECHNICAL DELIVERY CONDITIONS FOR ALLOY STEELS |
| DIN EN 764-4:2015-03 | PRESSURE EQUIPMENT - PART 4: ESTABLISHMENT OF TECHNICAL DELIVERY CONDITIONS FOR METALLIC MATERIALS |
| DIN EN 10083-1 E : 2006 | STEELS FOR QUENCHING AND TEMPERING - PART 1: GENERAL TECHNICAL DELIVERY CONDITIONS |
| BS EN 10297-1:2003 | Seamless circular steel tubes for mechanical and general engineering purposes. Technical delivery conditions Non-alloy and alloy steel tubes |
| EN 10084:2008 | Case hardening steels - Technical delivery conditions |
| EN 10089:2002 | Hot-rolled steels for quenched and tempered springs - Technical delivery conditions |
| ISO 6507-1:2005 | Metallic materials Vickers hardness test Part 1: Test method |
| ISO 6508-3:2015 | Metallic materials — Rockwell hardness test — Part 3: Calibration of reference blocks |
| ISO 6508-1:2016 | Metallic materials — Rockwell hardness test — Part 1: Test method |
| ISO 6508-2:2015 | Metallic materials — Rockwell hardness test — Part 2: Verification and calibration of testing machines and indenters |
Sorry this product is not available in your region.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.