EN ISO 1519:2011
Current
Current
The latest, up-to-date edition.
Paints and varnishes - Bend test (cylindrical mandrel) (ISO 1519:2011)
Published date
01-15-2011
Publisher
Foreword
Introduction
1 Scope
2 Normative references
3 Principle
4 Apparatus
5 Sampling
6 Test panels
7 Procedure
8 Expression of results
9 Precision
10 Test report
Bibliography
ISO 1519:2011 specifies an empirical test procedure for assessing the resistance of a coating of paint, varnish or related product to cracking and/or detachment from a metal or plastics substrate when subjected to bending round a cylindrical mandrel under standard conditions.For a multi-coat system, each coat can be tested separately or the complete system can be tested.The method specified can be carried out either as a “pass/fail” test, by carrying out the test with a single specified size of mandrel, to assess compliance with a particular requirement; or by repeating the procedure using successively smaller mandrels to determine the diameter of the first mandrel over which the coating cracks and/or becomes detached from the substrate.Two types of apparatus are specified, type 1 being appropriate for use on test panels of thickness up to 0,3 mm, and type 2 for use on test panels of thickness up to 1,0 mm. Both types of apparatus have been found to give similar results with the same coating, but normally only one will be used for testing a given product.
| Committee |
CEN/TC 139
|
| DocumentType |
Standard
|
| PublisherName |
Comite Europeen de Normalisation
|
| Status |
Current
|
| Standards | Relationship |
| SS-EN ISO 1519 : 2011 | Identical |
| SN EN ISO 1519:2011 | Identical |
| NBN EN ISO 1519 : 2011 | Identical |
| UNI EN ISO 1519 : 2011 | Identical |
| NS EN ISO 1519 : 2011 | Identical |
| UNE-EN ISO 1519:2011 | Identical |
| DIN EN ISO 1519:2011-04 | Identical |
| NEN EN ISO 1519 : 2011 | Identical |
| BS EN ISO 1519:2011 | Identical |
| ISO 1519:2011 | Identical |
| PN EN ISO 1519 : 2012 | Identical |
| NF EN ISO 1519 : 2011 | Identical |
| I.S. EN ISO 1519:2011 | Identical |
| I.S. EN 3840:2007 | AEROSPACE SERIES - PAINTS AND VARNISHES - TECHNICAL SPECIFICATION |
| NF EN 60464-2 : 2002 AMD 1 2006 | VARNISHES USED FOR ELECTRICAL INSULATION - PART 2: METHODS OF TEST |
| 17/30371343 DC : 0 | BS EN 4688 - AEROSPACE SERIES - PAINTS AND VARNISHES - CORROSION RESISTANT CHROMATED TWO COMPONENT COLD CURING EPOXY PRIMER - HIGH CORROSION RESISTANCE FOR MILITARY APPLICATION |
| DIN EN 15813:2011-06 | Polymer modified bituminous thick coatings for waterproofing - Determination of flexibility at low temperatures |
| I.S. EN 12206-1:2004 | PAINTS AND VARNISHES - COATING OF ALUMINIUM AND ALUMINIUM ALLOYS FOR ARCHITECTURAL PURPOSES - PART 1: COATINGS PREPARED FROM COATING POWDER |
| 17/30371344 DC : 0 | BS EN 4689 - AEROSPACE SERIES - PAINTS AND VARNISHES - TWO COMPONENTS COLD CURING POLYURETHANE FINISH - HIGH FLEXIBILITY AND CHEMICAL AGENT RESISTANCE FOR MILITARY APPLICATION |
| BS EN 3021:2017 | Aerospace series. Molybdenum disulphide dry film lubricants graphite and halogen free. Technical specification |
| BS EN 4687:2012 | Aerospace series. Paints and varnishes. Chromate free non corrosion inhibiting two components cold curing primer for military application |
| PREN 4689 : 200P1 | AEROSPACE SERIES - PAINTS AND VARNISHES - TWO COMPONENTS COLD CURING POLYURETHANE FINISH - HIGH FLEXIBILITY AND CHEMICAL AGENT RESISTANCE FOR MILITARY APPLICATION |
| PREN 3021 : DRAFT 2015 | AEROSPACE SERIES - MOLYBDENUM DISULPHIDE DRY FILM LUBRICANTS GRAPHITE AND HALOGEN FREE - TECHNICAL SPECIFICATION |
| DIN EN 1396:2015-06 | Aluminium and aluminium alloys - Coil coated sheet and strip for general applications - Specifications |
| BS EN 12206-1:2004 | Paints and varnishes. Coating of aluminium and aluminium alloys for architectural purposes Coatings prepared from coating powder |
| UNE-EN 505:2013 | Roofing products from metal sheet - Specification for fully supported roofing products of steel sheet |
| UNI EN 4689 : 2013 | AEROSPACE SERIES - PAINTS AND VARNISHES - TWO COMPONENTS COLD CURING POLYURETHANE FINISH - HIGH FLEXIBILITY AND CHEMICAL AGENT RESISTANCE FOR MILITARY APPLICATION |
| EN 13438:2013 | Paints and varnishes - Powder organic coatings for hot dip galvanised or sherardised steel products for construction purposes |
| EN 61086-2:2004 | Coatings for loaded printed wire boards (conformal coatings) - Part 2: Methods of test |
| 17/30371341 DC : 0 | PREN 4687 - AEROSPACE SERIES - PAINTS AND VARNISHES - CHROMATE FREE (NON CORROSION INHIBITING) TWO COMPONENT COLD CURING PRIMER - CHROMATE FREE PRIMER FOR MILITARY APPLICATION |
| BS EN 4689:2012 | Aerospace series. Paints and varnishes. Two components cold curing polyurethane finish. High flexibility and chemical agent resistance for military application |
| EN 12206-1:2004 | Paints and varnishes - Coating of aluminium and aluminium alloys for architectural purposes - Part 1: Coatings prepared from coating powder |
| BS EN 60464-2:2001 | Varnishes used for electrical insulation Methods of test |
| 13/30286946 DC : 0 | BS EN 1396 - ALUMINIUM AND ALUMINIUM ALLOYS - COIL COATED SHEET AND STRIP FOR GENERAL APPLICATIONS - SPECIFICATIONS |
| I.S. EN 4687:2012 | AEROSPACE SERIES - PAINTS AND VARNISHES - CHROMATE FREE NON CORROSION INHIBITING TWO COMPONENTS COLD CURING PRIMER FOR MILITARY APPLICATION |
| I.S. EN 3021:2017 | AEROSPACE SERIES - MOLYBDENUM DISULPHIDE DRY FILM LUBRICANTS GRAPHITE AND HALOGEN FREE - TECHNICAL SPECIFICATION |
| PREN 13523-7 : DRAFT 2012 | COIL COATED METALS - TEST METHODS - PART 7: RESISTANCE TO CRACKING ON BENDING (T-BEND TEST) |
| NF EN 12206-1 : 2011 | PAINTS AND VARNISHES - COATING OF ALUMINIUM AND ALUMINIUM ALLOYS FOR ARCHITECTURAL PURPOSES - PART 1: COATINGS PREPARED FROM COATING POWDER |
| DIN EN 13438:2013-12 | PAINTS AND VARNISHES - POWDER ORGANIC COATINGS FOR HOT DIP GALVANISED OR SHERARDISED STEEL PRODUCTS FOR CONSTRUCTION PURPOSES |
| DIN EN 15088 E : 2006 | ALUMINIUM AND ALUMINIUM ALLOYS - STRUCTURAL PRODUCTS FOR CONSTRUCTION WORKS - TECHNICAL CONDITIONS FOR INSPECTION AND DELIVERY |
| DIN EN 505:2013-06 | ROOFING PRODUCTS FROM METAL SHEET - SPECIFICATION FOR FULLY SUPPORTED ROOFING PRODUCTS OF STEEL SHEET |
| I.S. EN 13523-7:2014 | COIL COATED METALS - TEST METHODS - PART 7: RESISTANCE TO CRACKING ON BENDING (T-BEND TEST) |
| UNI EN 4688 : 2013 | AEROSPACE SERIES - PAINTS AND VARNISHES - CORROSION INHIBITING TWO COMPONENTS COLD CURING PRIMER FOR MILITARY APPLICATION |
| DIN EN 12206-1:2004-09 | Paints and varnishes - Coating of aluminium and aluminium alloys for architectural purposes - Part 1: Coatings prepared from coating powder |
| I.S. EN 505:2013 | ROOFING PRODUCTS FROM METAL SHEET - SPECIFICATION FOR FULLY SUPPORTED ROOFING PRODUCTS OF STEEL SHEET |
| I.S. EN 1396:2015 | ALUMINIUM AND ALUMINIUM ALLOYS - COIL COATED SHEET AND STRIP FOR GENERAL APPLICATIONS - SPECIFICATIONS |
| UNI EN 4687 : 2013 | AEROSPACE SERIES - PAINTS AND VARNISHES - CHROMATE FREE NON CORROSION INHIBITING TWO COMPONENTS COLD CURING PRIMER FOR MILITARY APPLICATION |
| EN 4689:2012 | Aerospace series - Paints and varnishes - Two components cold curing polyurethane finish - High flexibility and chemical agent resistance for military application |
| I.S. EN 13438:2013 | PAINTS AND VARNISHES - POWDER ORGANIC COATINGS FOR HOT DIP GALVANISED OR SHERARDISED STEEL PRODUCTS FOR CONSTRUCTION PURPOSES |
| EN 4687:2012 | Aerospace series - Paints and varnishes - Chromate free non corrosion inhibiting two components cold curing primer for military application |
| EN 4688:2012 | Aerospace series - Paints and varnishes - Corrosion inhibiting two components cold curing primer for military application |
| 12/30264367 DC : 0 | BS EN 505 - ROOFING PRODUCTS FROM METAL SHEET - SPECIFICATION FOR FULLY SUPPORTED ROOFING PRODUCTS OF STEEL SHEET |
| UNE-EN 15813:2011 | Polymer modified bituminous thick coatings for waterproofing - Determination of flexibility at low temperatures |
| DIN EN 15813 E : 2011 | POLYMER MODIFIED BITUMINOUS THICK COATINGS FOR WATERPROOFING - DETERMINATION OF FLEXIBILITY AT LOW TEMPERATURES |
| 17/30364785 DC : 0 | BS EN 4868 - AEROSPACE SERIES - ANODIC ELECTRODEPOSITION OF PRIMER |
| I.S. EN 4688:2012 | AEROSPACE SERIES - PAINTS AND VARNISHES - CORROSION INHIBITING TWO COMPONENTS COLD CURING PRIMER FOR MILITARY APPLICATION |
| BS EN 61086-2:2004 | Coatings for loaded printed wire boards (conformal coatings) Methods of test |
| I.S. EN 4689:2012 | AEROSPACE SERIES - PAINTS AND VARNISHES - TWO COMPONENTS COLD CURING POLYURETHANE FINISH - HIGH FLEXIBILITY AND CHEMICAL AGENT RESISTANCE FOR MILITARY APPLICATION |
| PREN 505 : DRAFT 2012 | ROOFING PRODUCTS FROM METAL SHEET - SPECIFICATION FOR FULLY SUPPORTED ROOFING PRODUCTS OF STEEL SHEET |
| CEI EN 61086-2 : 2005 | COATINGS FOR LOADED PRINTED WIRE BOARDS (CONFORMAL COATINGS) - PART 2: METHODS OF TEST |
| I.S. EN 60464-2:2002 | VARNISHES USED FOR ELECTRICAL INSULATION - PART 2: METHODS OF TEST |
| BS EN 1396:2007 | Aluminium and aluminium alloys. Coil coated sheet and strip for general applications. Specifications |
| UNI EN 505 : 2013 | ROOFING PRODUCTS FROM METAL SHEET - SPECIFICATION FOR FULLY SUPPORTED ROOFING PRODUCTS OF STEEL SHEET |
| UNI EN 13438 : 2013 | PAINTS AND VARNISHES - POWDER ORGANIC COATINGS FOR HOT DIP GALVANISED OR SHERARDIZED STEEL PRODUCTS FOR CONSTRUCTION PURPOSES |
| PREN 13438 : DRAFT 2012 | PAINTS AND VARNISHES - POWDER ORGANIC COATINGS FOR GALVANIZED OR SHERARDIZED STEEL PRODUCTS FOR CONSTRUCTION PURPOSES |
| PREN 4688 : 200P1 | AEROSPACE SERIES - PAINTS AND VARNISHES - CORROSION INHIBITING TWO COMPONENTS COLD CURING PRIMER FOR MILITARY APPLICATION |
| PREN 4687 : 200P1 | AEROSPACE SERIES - PAINTS AND VARNISHES - CHROMATE FREE NON CORROSION INHIBITING TWO COMPONENTS COLD CURING PRIMER FOR MILITARY APPLICATION |
| UNI EN 15813 : 2011 | POLYMER MODIFIED BITUMINOUS THICK COATINGS FOR WATERPROOFING - DETERMINATION OF FLEXIBILITY AT LOW TEMPERATURES |
| I.S. EN 61086-2:2004 | COATINGS FOR LOADED PRINTED WIRE BOARDS (CONFORMAL COATINGS) - PART 2: METHODS OF TEST |
| DIN EN 13523-7:2014-08 | Coil coated metals - Test methods - Part 7: Resistance to cracking on bending (T-bend test) |
| UNE-EN 1396:2015 | Aluminium and aluminium alloys - Coil coated sheet and strip for general applications - Specifications |
| BS EN 10301:2003 | Steel tubes and fittings for on and offshore pipelines. Internal coating for the reduction of friction for conveyance of non corrosive gas |
| BS EN 13438:2013 | Paints and varnishes. Powder organic coatings for hot dip galvanised or sherardised steel products for construction purposes |
| DIN EN 15088:2016-09 (Draft) | Aluminium and aluminium alloys - Structural products for construction works - Technical conditions for inspection and delivery; German and English version prEN 15088:2016 |
| BS EN 15088:2005 | Aluminium and aluminium alloys. Structural products for construction works. Technical conditions for inspection and delivery |
| EN 15088:2005 | Aluminium and aluminium alloys - Structural products for construction works - Technical conditions for inspection and delivery |
| EN 1396:2015 | Aluminium and aluminium alloys - Coil coated sheet and strip for general applications - Specifications |
| EN 15813:2011 | Polymer modified bituminous thick coatings for waterproofing - Determination of flexibility at low temperatures |
| EN 505:2013 | Roofing products from metal sheet - Specification for fully supported roofing products of steel sheet |
| EN 3840:2007 | Aerospace series - Paints and varnishes - Technical specification |
| EN 3021:2017 | Aerospace series - Molybdenum disulphide dry film lubricants graphite and halogen free - Technical specification |
| 12/30238456 DC : 0 | BS EN 13438 - PAINTS AND VARNISHES - POWDER ORGANIC COATINGS FOR GALVANIZED OR SHERARDIZED STEEL PRODUCTS FOR CONSTRUCTION PURPOSES |
| 12/30268961 DC : 0 | BS EN 13523-7 - COIL COATED METALS - TEST METHODS - PART 7: RESISTANCE TO CRACKING ON BENDING (T-BEND TEST) |
| BS EN 15813:2011 | Polymer modified bituminous thick coatings for waterproofing. Determination of flexibility at low temperatures |
| BS EN 4688:2012 | Aerospace series. Paints and varnishes. Corrosion inhibiting two components cold curing primer for military application |
| I.S. EN 15813:2011 | POLYMER MODIFIED BITUMINOUS THICK COATINGS FOR WATERPROOFING - DETERMINATION OF FLEXIBILITY AT LOW TEMPERATURES |
| 04/30125694 DC : DRAFT NOV 2004 | EN 15088 - ALUMINIUM AND ALUMINIUM ALLOYS - STRUCTURAL PRODUCTS FOR CONSTRUCTION WORKS - TECHNICAL CONDITIONS FOR INSPECTION AND DELIVERY |
| BS EN 3840:2007 | Aerospace series. Paints and varnishes. Technical specification |
| PREN 4868 : DRAFT 2018 | AEROSPACE SERIES - ANODIC ELECTRODEPOSITION OF HEXAVALENT CHROMIUM FREE PRIMER |
| PREN 3840 : 200P2 | AEROSPACE SERIES - PAINTS AND VARNISHES - TECHNICAL SPECIFICATION |
| PREN 1396 : DRAFT 2013 | ALUMINIUM AND ALUMINIUM ALLOYS - COIL COATED SHEET AND STRIP FOR GENERAL APPLICATIONS - SPECIFICATIONS |
| BS EN 505:2013 | Roofing products from metal sheet. Specification for fully supported roofing products of steel sheet |
| BS EN 13523-7:2014 | Coil coated metals. Test methods Resistance to cracking on bending (T-bend test) |
| EN 10301:2003 | Steel tubes and fittings for on and offshore pipelines - Internal coating for the reduction of friction for conveyance of non corrosive gas |
| EN 13523-7:2014 | Coil coated metals - Test methods - Part 7: Resistance to cracking on bending (T-bend test) |
| UNI EN 13523-7 : 2014 | COIL COATED METALS - TEST METHODS - PART 7: RESISTANCE TO CRACKING ON BENDING (T-BEND TEST) |
| EN 60464-2:2001/A1:2006 | VARNISHES USED FOR ELECTRICAL INSULATION - PART 2: METHODS OF TEST |
| DIN EN 15088:2006-03 | Aluminium and aluminium alloys - Structural products for construction works - Technical conditions for inspection and delivery; German version EN 15088:2005 |
| DIN EN 10301:2004-01 | Steel tubes and fittings for on and offshore pipelines - Internal coating for the reduction of friction for conveyance of non corrosive gas |
| ISO 1514:2016 | Paints and varnishes — Standard panels for testing |
| ISO 2808:2007 | Paints and varnishes Determination of film thickness |
| ISO 15528:2013 | Paints, varnishes and raw materials for paints and varnishes Sampling |
| ISO 1513:2010 | Paints and varnishes Examination and preparation of test samples |
| ISO 3270:1984 | Paints and varnishes and their raw materials — Temperatures and humidities for conditioning and testing |
Sorry this product is not available in your region.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.