Hose Assembly, Polytetrafluoroethylene, Para-Aramid Reinforced, 3000/4000 psi, 275 °F, Standard Duty, Hydraulic, Aircraft Systems
Hardcopy , PDF
English
05-02-2016
1. SCOPE
2. REFERENCES
3. TECHNICAL REQUIREMENTS
4. QUALITY ASSURANCE PROVISIONS
5. PREPARATION FOR DELIVERY
6. NOTES
This SAE Aerospace Standard (AS) defines the requirements for a polytetrafluoroethylene (PTFE) lined, para-aramid fiber reinforced, hose assembly suitable for use up to 4000 psi, and up to 275 °F, aircraft and missile hydraulic and pneumatic systems.
Committee |
G-3
|
DocumentType |
Revision
|
Pages |
26
|
PublisherName |
SAE International
|
Status |
Current
|
Supersedes |
SAE AIR 5693 : 2014 | COMPATIBILITY OF PTFE HOSE ASSEMBLIES WITH TYPICAL FLUIDS FOUND IN AEROSPACE APPLICATIONS |
MIL-H-5440 Revision H:1993 | HYDRAULIC SYSTEMS, AIRCRAFT, TYPES 1 AND 11 DESIGN AND INSTALLATION REQUIREMENTS FOR |
SAE AS 150 : 2017 | HOSE ASSEMBLY, TYPE CLASSIFICATIONS OF, BASIC PERFORMANCE AND FIRE RESISTANCE |
SAE AMS 2486 : 2010 | CONVERSION COATING OF TITANIUM ALLOYS FLUORIDE-PHOSPHATE TYPE |
SAE AS 4582 : 2015 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 4000 PSI, 275 DEGREES F, TITANIUM FITTINGS, FLARELESS, STRAIGHT TO 90 DEGREES |
SAE AS 4584 : 2015 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 4000 PSI, 275 DEGREES F, TITANIUM FITTINGS, FLARELESS, 45 DEGREES TO 45 DEGREES |
SAE AMS5659S : 2016 | Steel, Corrosion-Resistant, Bars, Wire, Forgings, Rings, and Extrusions 15Cr - 4.5Ni - 0.30Cb (Nb) - 3.5Cu<br> |
SAE AMS 5645 : 2016 | STEEL, CORROSION AND HEAT RESISTANT, BARS, WIRE, FORGINGS, TUBING, AND RINGS, 18CR - 10NI - 0.40TI (321), SOLUTION HEAT TREATED |
SAE ARP 1835 : 2013 | PREPARATION FOR DELIVERY, GENERAL REQUIREMENTS FOR HOSE ASSEMBLIES |
SAE AS 611F : 2010 | HOSE ASSEMBLY AND TUBING, POLYTETRAFLUOROETHYLENE, CLEANING METHODS FOR |
ASTM A 262 : 2015 : REDLINE | Standard Practices for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steels |
SAE AS 4703 : 2015 | FITTING END, ACORN, SHORT FLARELESS, DESIGN STANDARD |
SAE AS 4574 : 2015 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 3000 PSI, 275 DEGREE F, TITANIUM FITTINGS, BEAM SEAL, STRAIGHT TO STRAIGHT |
ASTM B 348 : 2013 : REDLINE | Standard Specification for Titanium and Titanium Alloy Bars and Billets |
SAE AS 603 : 2015 | IMPULSE TESTING OF HYDRAULIC HOSE, TUBING, AND FITTING ASSEMBLIES |
NAS1760:2015 | FITTING END, FLARELESS ACORN, STANDARD DIMENSIONS FOR |
SAE AS 4591 : 2015 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 4000 PSI, 275 DEGREES F, TITANIUM FITTINGS, BEAM SEAL, 90 DEGREES TO 90 DEGREES |
SAE AMS 5571J:2012(R2018) | STEEL, CORROSION AND HEAT-RESISTANT, SEAMLESS TUBING, 18CR - 10.5NI - 0.70CB (NB) (347), SOLUTION HEAT TREATED |
SAE AMS 5643 : 2016 | STEEL, CORROSION-RESISTANT, BARS, WIRE, FORGINGS, MECHANICAL TUBING, AND RINGS, 16CR - 4.0NI - 0.30CB (NB) - 4.0CU, SOLUTION HEAT TREATED, PRECIPITATION HARDENABLE |
SAE AS 4578 : 2015 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 3000 PSI, 275 DEGREES F, TITANIUM FITTINGS, BEAM SEAL, 45 DEGREES TO 90 DEGREES |
SAE AS 4395 : 2013 | FITTING END, FLARED, TUBE CONNECTION, DESIGN STANDARD |
SAE AMS 5743 : 2014 | STEEL, CORROSION AND HEAT-RESISTANT, BARS AND FORGINGS 15.5CR - 4.5NI - 2.9MO - 0.10N SOLUTION HEAT TREATED, SUB-ZERO COOLED, EQUALIZED, AND OVER-TEMPERED |
SAE AMS 5561 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, WELDED AND DRAWN OR SEAMLESS AND DRAWN TUBING, 9.0MN - 20CR - 6.5NI - 0.28N, HIGH-PRESSURE HYDRAULIC |
SAE AS 1055 : 2013 | FIRE TESTING OF FLEXIBLE HOSE, TUBE ASSEMBLIES, COILS, FITTINGS AND SIMILAR SYSTEM COMPONENTS |
SAE AS 1073B : 2013(S2019) | SLEEVE HOSE ASSEMBLY, HEAT SHRINKABLE |
ASME B46.1 : 2009 | SURFACE TEXTURE (SURFACE ROUGHNESS, WAVINESS, AND LAY) |
SAE AS 85421/1 : 2002 | FITTING END, STANDARD DIMENSIONS FOR DYNAMIC BEAM SEAL, MALE |
SAE AS 4658 : 2013 | FITTING END, EXTERNAL THREAD, SHORT FLARELESS, DESIGN STANDARD |
SAE AMS 5647 : 2017 | STEEL, CORROSION-RESISTANT, BARS, WIRE, FORGINGS, MECHANICAL TUBING, AND RINGS, 19CR - 9.5NI, SOLUTION HEAT TREATED |
MIL-PRF-680 Revision C:2010 | DEGREASING SOLVENT |
SAE AS 4589 : 2001 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 4000 PSI, 275 DEGREES F, TITANIUM FITTINGS, BEAM SEAL, 45 DEGREES TO 45 DEGREES |
SAE ARP 908 : 2013 | TORQUE REQUIREMENTS, INSTALLATION AND QUALIFICATION TEST, HOSE AND TUBE FITTING |
SAE AS 4702 : 2015 | NUT, RETAINED, SHORT FLARELESS |
SAE AMS 4965 : 2014 | TITANIUM ALLOY, BARS, WIRE, FORGINGS, AND RINGS, 6.0AL 4.0V, SOLUTION HEAT TREATED AND AGED |
MIL-PRF-87257 Revision C:2017 | HYDRAULIC FLUID, FIRE RESISTANT, LOW TEMPERATURE, SYNTHETIC HYDROCARBON BASE, AIRCRAFT AND MISSILE |
SAE AS 7003 : 2008 | NADCAP PROGRAM REQUIREMENTS |
SAE AS 7112 : 1997 | NATIONAL AEROSPACE AND DEFENSE CONTRACTORS ACCREDITATION PROGRAM REQUIREMENTS FOR FLUID SYSTEM COMPONENTS |
SAE AMS 5567 : 2015 | STEEL, CORROSION RESISTANT, SEAMLESS OR WELDED HYDRAULIC TUBING, 19CR - 10NI (304), SOLUTION HEAT TREATED |
SAE AS 5272 : 2016 | LUBRICANT, SOLID FILM, HEAT CURED, CORROSION INHIBITING, PROCUREMENT SPECIFICATION |
SAE AIR 1228 : 2009 | STANDARD IMPULSE MACHINE EQUIPMENT AND OPERATION |
SAE AS 4575 : 2015 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 3000 PSI, 275 DEGREE F, TITANIUM FITTINGS, BEAM SEAL, STRAIGHT TO 45 DEGREES |
SAE AMS 5637 : 2012 | STEEL, CORROSION RESISTANT, BARS AND WIRE 18CR - 9.0NI (SAE 30302) SOLUTION HEAT TREATED, COLD DRAWN AND STRESS RELIEVED 125 KSI (862 MPA) TENSILE STRENGTH |
SAE AMS 5646 : 2014 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS, TUBING, AND RINGS, 18CR - 11NI - 0.60CB(NB) (347), SOLUTION HEAT TREATED |
SAE AS 4568 : 2015 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 3000 PSI, 275 DEGREE F, TITANIUM FITTINGS, FLARELESS, STRAIGHT TO STRAIGHT |
SAE AS 85421 : 2015 | FITTINGS, TUBE, FLUID SYSTEMS, SEPARABLE, BEAM SEAL, 3000/4000 PSI, GENERAL SPECIFICATION FOR |
SAE AS 4579 : 2015 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 3000 PSI, 275 DEGREES F, TITANIUM FITTINGS, BEAM SEAL, 90 DEGREES TO 90 DEGREES |
SAE AMS QQ S 763D : 2013(S2015) | STEEL, CORROSION RESISTANT, BARS, WIRE, SHAPES, AND FORGINGS |
SAE AS 4572 : 2015 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 3000 PSI, 275 DEGREE F, TITANIUM FITTINGS, FLARELESS, 45 DEGREE TO 45 DEGREE |
SAE AS 4580 : 2001 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 4000 PSI, 275 DEGREES F, TITANIUM FITTINGS, FLARELESS, STRAIGHT TO STRAIGHT |
SAE AS 4700 : 1992 | SHORT FLARELESS FITTINGS, INSTALLATION PROCEDURES AND TORQUE FOR |
SAE AMS 4945 : 2014 | TITANIUM ALLOY TUBING, SEAMLESS, HYDRAULIC 3AL - 2.5V, CONTROLLED CONTRACTILE STRAIN RATIO COLD WORKED, STRESS RELIEVED |
AWS D17.1 : 2001 | SPECIFICATION FOR FUSION WELDING FOR AEROSPACE APPLICATIONS |
SAE AS 8879 : 2004 | SCREW THREADS - UNJ PROFILE, INCH CONTROLLED RADIUS ROOT WITH INCREASED MINOR DIAMETER |
SAE AMS 4921 : 2016 | TITANIUM BARS, WIRE, FORGINGS, AND RINGS COMMERCIALLY PURE, 70 KSI (483 MPA) YIELD STRENGTH |
SAE AS 1072F : 2013(S2019) | SLEEVE, HOSE ASSEMBLY, FIRE PROTECTION |
SAE AMS 5575 : 2013 | STEEL, CORROSION AND HEAT-RESISTANT, WELDED TUBING, 18CR - 10.5NI - 0.70CB (NB) (347), SOLUTION HEAT TREATED |
SAE AS 4583 : 2015 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 4000 PSI, 275 DEGREES F, TITANIUM FITTINGS, FLARELESS, 45 DEGREES TO 90 DEGREES |
SAE AS 4588 : 2001 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 4000 PSI, 275 DEGREES F, TITANIUM FITTINGS, BEAM SEAL, STRAIGHT TO 90 DEGREES |
SAE AMS 5570 : 2013 | STEEL, CORROSION AND HEAT-RESISTANT, SEAMLESS TUBING 18CR - 11NI - 0.40TI (321), SOLUTION HEAT TREATED |
SAE AS 4577 : 2015 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 3000 PSI, 275 DEGREES F, TITANIUM FITTINGS, BEAM SEAL, 45 DEGREES TO 45 DEGREES |
SAE AS 2078 : 2015 | TEST METHODS, HOSE ASSEMBLIES, POLYTETRAFLUOROETHYLENE (PTFE) |
SAE AS 4570 : 2015 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 3000 PSI, 275 DEGREE F, TITANIUM FITTINGS, FLARELESS, STRAIGHT TO 90 DEGREE |
SAE AS 1241 : 2016 | FIRE RESISTANT PHOSPHATE ESTER HYDRAULIC FLUID FOR AIRCRAFT |
SAE AS 4590 : 2001 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 4000 PSI, 275 DEGREES F, TITANIUM FITTINGS, BEAM SEAL, 45 DEGREES TO 90 DEGREES |
SAE AMS 2700E : 2011 | PASSIVATION OF CORROSION RESISTANT STEELS |
MIL-PRF-83282 Revision D:1997 | HYDRAULIC FLUID, FIRE RESISTANT, SYNTHETIC HYDROCARBON BASE, METRIC, NATO CODE NUMBER H-537 |
SAE AMS 5639 : 2017 | STEEL, CORROSION-RESISTANT, BARS, WIRE, FORGINGS, MECHANICAL TUBING, AND RINGS, 19CR - 10NI, SOLUTION HEAT TREATED |
MIL F 8815 : D | FILTER AND FILTER ELEMENTS, FLUID PRESSURE, HYDRAULIC LINE, 15 MICRON ABSOLUTE AND 5 MICRON ABSOLUTE, TYPE 11 SYSTEMS; GENERAL SPECIFICATION FOR |
SAE AS 33514 : 2015 | FITTING END, STANDARD DIMENSIONS FOR FLARELESS TUBE CONNECTION AND GASKET SEAL |
SAE AS 4585 : 2001 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 4000 PSI, 275 DEGREES F, TITANIUM FITTINGS, FLARELESS, 90 DEGREES TO 90 DEGREES |
SAE AS 4375 : 2013 | FITTING END, FLARELESS, DESIGN STANDARD |
SAE AS 150 : 2014 | HOSE ASSEMBLY, TYPE CLASSIFICATIONS OF, BASIC PERFORMANCE AND FIRE RESISTANCE |
SAE AS 4488 : 2013 | TUBULAR ASSEMBLIES, FUSION WELDED, INSPECTION PROCESSES AND ACCEPTANCE STANDARDS FOR |
SAE AS 4659 : 2013 | FITTING END, BULKHEAD, EXTERNAL THREAD, SHORT FLARELESS, DESIGN STANDARD |
SAE AS 4581 : 2001 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 4000 PSI, 275 DEGREES F, TITANIUM FITTINGS, FLARELESS, STRAIGHT TO 45 DEGREES |
SAE AS 4571 : 2015 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 3000 PSI, 275 DEGREE F, TITANIUM FITTINGS, FLARELESS, 45 DEGREE TO 90 DEGREE |
SAE AMS 5636 : 2006 | STEEL, CORROSION-RESISTANT, BARS AND WIRE, 18CR - 9.0NI (SAE 30302), SOLUTION HEAT TREATED AND COLD DRAWN, 100 KSI (689 MPA) TENSILE STRENGTH |
SAE AS 4587 : 2001 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 4000 PSI, 275 DEGREES F, TITANIUM FITTINGS, BEAM SEAL, STRAIGHT TO 45 DEGREES |
ASME Y14.100 : 2017 | ENGINEERING DRAWING PRACTICES - ENGINEERING DRAWING AND RELATED DOCUMENTATION PRACTICES |
SAE AS 4576 : 2015 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 3000 PSI, 275 DEGREES F, TITANIUM FITTINGS, BEAM SEAL, STRAIGHT TO 90 DEGREES |
SAE AS 4573 : 2015 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 3000 PSI, 275 DEGREE F, TITANIUM FITTINGS, FLARELESS, 90 DEGREE TO 90 DEGREE |
ASTM D 638 : 2014 : REDLINE | Standard Test Method for Tensile Properties of Plastics |
SAE AS 4586 : 2001 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 4000 PSI, 275 DEGREES F, TITANIUM FITTINGS, BEAM SEAL, STRAIGHT TO STRAIGHT |
SAE AMS 5576 : 2005 | STEEL, CORROSION AND HEAT RESISTANT, WELDED TUBING - 18CR - 10.5NI - 0.40TI (SAE 30321) SOLUTION HEAT TREATED |
SAE AMS 5556 : 2016 | STEEL, CORROSION AND HEAT-RESISTANT, SEAMLESS OR WELDED HYDRAULIC TUBING 18CR - 11NI - 0.70CB (347) SOLUTION HEAT TREATED |
SAE AS 4569 : 2015 | HOSE ASSEMBLY, PTFE, PARA-ARAMID REINFORCED, STANDARD DUTY, 3000 PSI, 275 DEGREE F, TITANIUM FITTINGS, FLARELESS, STRAIGHT TO 45 DEGREE |
SAE AMS 4928 : 2016 | TITANIUM ALLOY BARS, WIRE, FORGINGS, RINGS, AND DRAWN SHAPES, 6AL - 4V, ANNEALED |
NAS847:2012 | CAPS AND PLUGS, PROTECTIVE, DUST AND MOISTURE SEAL |
SAE AS 4660 : 2013 | NUT, SHORT FLARELESS |
SAE AMS 5557 : 2012 | STEEL, CORROSION AND HEAT RESISTANT, SEAMLESS OR WELDED HYDRAULIC TUBING, 18.5CR - 10.5NI - 0.40TI (SAE 30321), SOLUTION HEAT TREATED |
Please Login or Create an Account so you can add users to your Multi user PDF Later.
Important note : All end users must be registered with an Account prior to user licenses being assigned.
Users cannot be edited or removed once added to your Multi user PDF.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.